This study aimed to assess whether the gender of the dental practitioner affects operative techniques in class 2 and class 5 resin composite restorations. In 2008, a nationwide survey was given to Korean dentists. Total 12,193 e-mails were distributed, 2,632 were opened by recipients, and 840 responses were collected. Of the respondents, 78.9% were male and 21.1% were female. The gender distribution in the age groups between respondents and the total population did not differ (p > 0.05). A chi-square test was used to compare technical differences between female and male dentists. A multiple logistic regression analysis was performed to assess the association between gender and operative techniques in resin composite restoration. For class 2 resin composite restoration, female dentists were 1.87 times more likely than male dentists to do multiple incremental fillings (four layers or more) and 2.72 times more likely than males to spend 30 minutes or more for the treatment (p < 0.05). For class 5 resin composite restoration, female dentists were 2.69 times more likely than their male counterparts to use a cavity base or liner, 1.83 times more likely to do multiple incremental fillings (four layers or more) and 1.63 times more likely to spend 20 minutes or more for the procedure (p < 0.05). The gender factor was influential to individual operative techniques in restorative treatment.

The purpose of this study was to perform quantitative comparisons of water permeable zones in both the adhesive and the hybrid layer before and after thermocycling in order to assess the integrity of the bonding interface. Twenty eight flat dentin surfaces were bonded with a light-cured composite resin using one of four commercial adhesives [OptiBond FL (OP), AdheSE (AD), Clearfil SE Bond (CL), and Xeno III (XE)]. These were sectioned into halves and subsequently cut to yield 2-mm thick specimens; one specimen for control and the other subjected to thermocycling for 10,000 cycles. After specimens were immersed in ammoniacal silver nitrate for 24 h and exposed to a photo developing solution for 8 h, the bonded interface was analyzed by scanning electron microscopy (SEM) and wavelength dispersive spectrometry (WDS) at five locations per specimen. Immediately after bonding, the adhesive layer of OP showed the lowest silver uptake, followed by CL, AD, and XE in ascending order (p < 0.0001); the hybrid layer of CL had the lowest silver content among the groups (p = 0.0039). After thermocycling, none of the adhesives manifested a significant increase of silver in either the adhesive or the hybrid layer. SEM demonstrated the characteristic silver penetrated patterns within the interface. It was observed that integrity of bonding was well maintained in OP and CL throughout the thermocycling process. Adhesive-tooth interfaces are vulnerable to hydrolytic degradation and its permeability varies in different adhesive systems, which may be clinically related to the restoration longevity.