Clinical suggestion for the limitation of application time of NaOCl solution is needed to avoid large reductions in resin-dentin bond strength. The aim of this study was to measure the change of µ-tensile bond strength after the various application time of 5.25% NaOCl solution to pulp chamber dentin in endodontic access cavity, and to evaluate the effect of 10% sodium ascorbate application for 10 min on bond strength after the treatment of 5.25% NaOCl solution. In this experiment, there were no statistical differences(p>0.05) in bond strengths between upper chamber dentin and lower chamber dentin. NaOCl-treated group for 20 min did not show any significant decrease(p>0.05) in bond strength than non-treated control group. In contrast to that, bond strengths of NaOCl-treated groups for 40 & 80 min were significantly lower(p<0.05) than that of non-treated control group.

10% sodium ascorbate retreated group for 10 min after 5.25% NaOCl application for 40 min to chamber dentin showed the recovery of bond strength significantly. However, the bond strength of sodium ascorbate retreated group after 5.25% NaOCl application for 80 min was still significantly lower(p<0.05) compared to the non-treated control group, which means the reductions in resin-dentin bond strength were not fully reversed. On the contrary, sodium ascorbate retreated group after 5.25% NaOCl application for 5 min showed significantly higher(p<0.05) bond strength compared to the control group, which demonstrates its superior recovery effect. In SEM exminations of specimens retreated with 10% sodium ascorbate after NaOCl application for 40 & 80 min showed that resin tags were formed clearly and densely, but weakly in density and homogeneity of individual resin tag compared to the control specimen.

The purpose of this study was to evaluate the influence of sodium ascorbate on microtensile bond strengths of total-etching adhesive system to pulp chamber dentin treated with NaOCl.

Pulp chambers of extracted human non-caries permanent molars were treated as follows: group 1, with 0.9% NaCl; group 2, with 5.25% NaOCl; group 3, with 5.25% NaOCl and 10% sodium ascorbate for 1min; group 4, with 5.25% NaOCl and 10% sodium ascorbate for 1 min and 10ml of water; group 5, with 5.25% NaOCl and 10% sodium ascorbate for 5 min; group 6, with 5.25% NaOCl and 10% sodium ascorbate for 5 min and 10ml of water; group 7, with 5.25% NaOCl and 10% sodium ascorbate for 10 min; group 8, with 5.25% NaOCl and 10% sodium ascorbate for 10 min and 10ml of water. Treated specimens were dried, bonded with a total-etching adhesive system (Single bond), restored with a composite resin(Z250) and kept for 24h at 100% humidity to measure the microtensile bond strength.

NaOCl-treated group (group 2) demonstrated significantly lower strength than the other groups. No significant difference in microtensile bond strengths was found between NaCl-treated group (group 1) and sodium ascorbate-treated groups (group 3-8). The results of this study indicated that dentin treated with NaOCl reduced the microtensile bond strength of Single bond. Application of 10% sodium ascorbate restored the bond strength of Single bond on NaOCl-treated dentin. Application time of sodium ascorbate did not have a significant effect.

This study was to verify that the combined application of NaOCl and EDTA was more effective in removal of smear layer than the application of NaOCl alone. Furthermore it was aimed to find out the optimal time for the application of EDTA.

Thirty five single rooted teeth were cleaned and shaped. NaOCl solution was used as an irrigant during instrumentation. After instrumentation, root canals of the control group were irrigated with 5 ml of NaOCl for 2 minutes. 30 sec, 1 min, and 2 min group were irrigated with 5 ml of 17% EDTA for 30 sec, 1 min, and 2 min respectively. Then the roots were examined with scanning electron microscopy for evaluating removal of smear layer and erosion of dentinal tubule.

The results were as follows;

The control group:

The smear layer was not removed at all.

The results suggest that 2 min application of 17% EDTA should be adequate to remove smear layer on both apical⅓ and middle⅓.

The purpose of this study was to compare the sealing ability of root canal obturation with or without the treatment of smear layer. Eighty extracted human teeth with one canal were selected. Instrumentation was performed with crown-down technique. After instrumentation, root canals of the NaOCl group and NaOCl-6 group were irrigated with 3% NaOCl. EDTA group and EDTA-6 group were irrigated with 17% EDTA. Then all teeth were obturated using continuous wave obturation technique.

NaOCl group and EDTA group were immersed in methylene blue solution for 84hours. NaOCl-6 group and EDTA-6 group were immersed in methylene blue solution for 6months. The teeth were sectioned at 1.5 mm (Level 1), 3.0 mm (Level 2) and 4.5 mm (Level 3) from the root apex. The length of dye-penetrated interface and the circumferential length of canal at each level were measured using Sigma-Scan Pro 5.0.

The mean leakage ratio was decreased cervically.

A variety files made of stainless steel (S-S) or nickel-titanium (Ni-Ti) are used during endodontic treatment. The purpose of this study was to evaluate the corrosion susceptibility of S-S and Ni-Ti endodontic files. Three brands of files were used for this study: K-flex® S-S files (Maillefer, USA), Profile® Ni-Ti files (Maillefer, USA), K-3® Ni-Ti files (SybronEndo, USA). 120 files of each brands (21mm, ISO size #20) were divided into 12 groups according to 1) sterilization methods using Autoclave or Ethylene Oxide (E-O) gas, 2) Irrigation solutions using 5.25 % NaOCl or Saline, 3) the number of sterilization (1, 5, 10 times). After above procedures, each of the files was inspected by three examiners with a light microscope and camera at X25. Each file was judged and ranked according to the following criteria: 0; no corrosion, 1; mild corrosion, 2; moderate corrosion, and 3; severe corrosion. The files of high score were examined under the Scanning Electron Microscope.

Data were statistically analyzed with the Kruskal-Wallis test (p < 0.05). Most of the ten time-autoclaved files had showed mild to moderate corrosion. But, one or five time-autoclaved files did not show corrosive surface. NaOCl treatment and E-O gas sterilization did not influence on corrosion. There was a significant difference in corrosion susceptibility between sterilization methods and the number of autoclaving. However, there was no significant difference between brands and file materials.