The purpose of this study was to evaluate the effect of pre-heating on some physical properties of composite resin.

Eighty extracted, noncarious human molars were used in the present study. Four different temperatures of composite resin were used: 4℃, 17℃, 48℃, and 56℃. The 4℃ and 17℃ values represented the refrigerator storage temperature and room temperature respectively. For 48℃ and 56℃, composite resin was heated to the temperatures. As physical properties of composite resin, shear bond strength, microhardness, and degree of conversion were measured. The data for each group were subjected to one-way ANOVAs followed by the Tukey's HSD test at 95% confidence level.

Both in enamel and dentin, among composite resin of 4℃, 17℃, 48℃, and 56℃, the pre-heated composite resin up to 56℃ revealed the highest shear bond strength, and pre-heated composite resin to the higher temperature revealed higher shear bond strength.

Microhardness value was also higher with composite resin of higher temperature.

Degree of conversion was also higher with composite resin of the higher temperature.

In this study, it seems that pre-heating composite resin up to the higher temperature may show higher shear bond strength, higher microhardness value, and higher degree of conversion. Therefore, when using composite resin in the clinic, preheating the composite resin could be recommended to have enhanced physical properties of it.

The purpose of this study was to evaluate the effect of thickness, filling methods and curing methods on the polymerization of dual cured core materials by means of microhardness test.

Two dual cured core materials, MultiCore Flow (Ivoclar Vivadent AG, Schaan, Liechtenstein) and Bis-Core (Bisco Inc., Schaumburg, IL, USA) were used in this study. 2 mm (bulky filled), 4 mm (bulky filled), 6 mm (bulky and incrementally filled) and 8 mm (bulky and incrementally filled)-thickness specimens were prepared with light cure or self cure mode. After storage at 37℃ for 24 hours, the Knoop hardness values (KHN) of top and bottom surfaces were measured and the microhardness ratio of top and bottom surfaces was calculated. The data were analyzed using one-way ANOVA and Scheffe multiple comparison test, with α = 0.05.

The effect of thickness on the polymerization of dual cured composites showed material specific results. In 2, 4 and 6 mm groups, the KHN of two materials were not affected by thickness. However, in 8 mm group of MultiCore Flow, the KHN of the bottom surface was lower than those of other groups (p < 0.05). The effect of filling methods on the polymerization of dual cured composites was different by their thickness or materials. In 6 mm thickness, there was no significant difference between bulk and incremental filling groups. In 8 mm thickness, Bis-Core showed no significant difference between groups. However, in MultiCore Flow, the microhardness ratio of bulk filling group was lower than that of incremental filling group (p < 0.05). The effect of curing methods on the polymerization of dual cured composites showed material specific results. In Bis-Core, the KHN of dual cured group were higher than those of self cured group at both surfaces (p < 0.05). However, in MultiCore Flow, the results were not similar at both surfaces. At the top surface, dual cured group showed higher KHN than that of self cured group (p < 0.05). However, in the bottom surface, dual cured group showed lower value than that of self cured group (p < 0.05).

The purinoreceptor, P2X₃ is a ligand-gated cation channel activated by extracellular ATP. It has been reported that ATP can be released during inflammation and tissue damage, which in turn may activate P2X₃ receptors to initiate nociceptive signals. However, little is known about the contribution of P2X₃ to the dental pain during pulpal inflammation. Therefore, the purpose of this study was to investigate the expression of P2X₃ and its colocalization with TRPV1 to understand the mechanism of pain transmission through P2X₃ in the human dental pulp with double labeling immunofluorescence method.

In the human dental pulp, intense P2X₃ immunoreactivity was observed throughout the coronal and radicular pulp. Of all P2X₃-positive fibers examined, 79.4% coexpressed TRPV1.

This result suggests that P2X₃ along with TRPV1 may be involved in the transmission of pain and potentiation of noxious stimuli during pulpal inflammation.

Recently, self-etching adhesive system has been introduced to simplify the clinical bonding procedures. It is less acidic compared to the phosphoric acid, thus there is doubt whether this system has enough bond strength to enamel. The purpose of this study was to investigate the influence of additional etching on the adhesion of resin composite to enamel.

Ninety extracted bovine permanent anterior teeth were used. The labial surfaces of the crown were ground with 600-grit abrasive paper under wet condition. The teeth were randomly divided into six groups of 15 teeth each. Clearfil SE Bond®, Adper™ Prompt L-Pop and Tyrian SPE™ were used as self-etching primers. Each self-etching primers were applied in both enamel specimens with and without additional etching. For additional etching groups, enamel surface was pretreated with 32% phosphoric acid (UNI-ETCH, Bisco, Inc., Schaumburg, IL, USA). Hybrid resin composite Clearfil AP-X, (Kuraray Co., Ltd., Osaka, Japan) was packed into the mold and light-cured for 40 seconds. Twenty-four hours after storage, the specimens were tested in shear bond strength. The data for each group were subjected to independent t - test at p < 0.01 to make comparisons among the groups.

In Clearfil SE Bond®, shear bond strength of additional etching group was higher than no additional etching group (p < 0.01). In Adper™ Prompt L-Pop and Tyrian SPE, there were no significant difference between additional etching and non-etching groups (p > 0.01).

In conclusion, self-etching adhesive system with weak acid seems to have higher bond strength to enamel with additional etching, while self-etching adhesive system with strong acid seems not.

The purpose of this study was to evaluate the influence of the AH-26 root canal sealer on the shear bond strength of composite resin to dentin.

One hundred and forty four (144) extracted, sound human molars were used. After embedding in a cylindrical mold, the occlusal part of the anatomical crown was cut away and trimmed in order to create a flat dentin surface. The teeth were randomly divided into three groups; the AH-26 sealer was applied to the AH-26 group, and zinc-oxide eugenol (ZOE) paste was applied to the ZOE group. The dentin surface of the control group did not receive any sealer.

A mount jig was placed against the surface of the teeth and the One-step dentin bonding agent was applied after acid etching. Charisma composite resin was packed into the mold and light cured. After polymerization, the alignment tube and mold were removed and the specimens were placed in distilled water at 37℃ for twenty four hours. The shear bond strength was measured by an Instron testing machine. The data for each group were subjected to one-way ANOVA and Tukey's studentized rank test so as to make comparisons between the groups.

The AH-26 group and the control group showed significantly higher shear bond strength than the ZOE group (p < 0.05).

There were no significant differences between the AH-26 group and the control one (p > 0.05).

Under the conditions of this study, the AH-26 root canal sealer did not seem to affect the shear bond strength of the composite resin to dentin while the ZOE sealer did. Therefore, there may be no decrease in bond strength when the composite resin core is built up immediately after a canal filling with AH-26 as a root canal sealer.

To evaluate the effect of vital tooth bleaching agent and alcohol pretreatment on dentin bonding, flat dentin windows were produced on the buccal side of the crowns of fifty-five extracted, human premolars. A bleaching gel, Opalescence® with 10% of carbamide peroxide (Ultradent Product, USA) was daily applied on the teeth of three experimental groups for six hours for 10 consecutive days, while teeth of a control group were not bleached. After 6 hours of bleaching gel application, the specimens were washed and stored in saline until the next day application. After application of One-step® dentin bonding agent (Bisco, USA), Z-250® resin (3M-ESPE, USA) was bonded to dentin with a mount jig. Shear bond strength was measured with an Instron machine (Type 4202, Instron Corp., USA) after 24 hours. The results were analyzed using one-way ANOVA and Duncan's multiple range test at p < 0.05.

Immediate bonding group showed significantly lower bond strength than un-bleached control group (p < 0.05).

Ethanol-treated group showed significantly higher bond strength compared to immediate bonding group (p < 0.05). However, the bond strength of the ethanol treatment group was lower than that of the un-bleached control group (p < 0.05).

There were no significant difference in shear bond strength between the 2-week delayed bonding group and the ethanol-treated group (p > 0.05) and between delayed bonding group and un-bleached control group (p > 0.05).

In the condition of the present study, it seems that alcohol pretreatment after bleaching procedure can reduce the adverse effect of vital bleaching agent on dentin bonding.

To evaluate the ratio of gutta-percha area in the canal after canal obturation with Continuous Wave of Condensation Technique (CWCT) with varying depths of plugger penetration, forty root canals of extracted human teeth were prepared up to size 40 of 0.06 taper with ProFile®. Canals of three groups were filled with CWCT with System B™ (Analytic Tech., USA) and different plugger penetration depths of 3, 5, or 7 mm from the apex. Canals of one group were filled with lateral condensation technique as a control. The filled teeth were cross-sectioned at 1, 2, and 3 mm levels from the apical foramen. The ratio of gutta-percha area in the canal was analyzed using Auto®Cad 2000. Data were analyzed with one-way ANOVA and Duncan's multiple range test.

At all levels, higher gutta-percha area ratio was found with deeper plugger penetration depth in CWCT, and cold lateral condensation group showed higher ratio than group of plugger penetration to apical 7 mm in CWCT.

At apical 1 mm and 2 mm levels, group of plugger penetration to apical 3 mm showed significantly higher gutta-percha area ratio than those of apical 7 mm and lateral condensation (p < 0.05).

It is concluded therefore that, under the conditions of the present study, deeper plugger penetration depth results in more favorable and efficient obturation in CWCT.

To evaluate the change of working length with various instrumentation techniques in curved canals, working length and canal curvature were determined before and after canal instrumentation in buccal or mesial canals of extracted human molars. Stainless steel K-files (MANI®, Matsutani Seisakusho Co. Takanezawa, Japan), nickel-titanium K-files (Naviflex NT™, Brassler, Savannah, USA), ProFile®, and ProTaper™ (Dentsply-Maillefer, Ballaigues, Switzerland) were used to prepare the canals with crown-down technique. In two hand instrumentation groups, coronal flaring was made with Gates Glidden burs. Apical canals were instrumented until apical diameter had attained a size of 30. Positional relation between the tooth apex and the #10 K-file tip was examined by using AutoCAD 2000 (Autodesk Corp., San Rafael. CA, USA) under a stereomicroscope before and after coronal flaring, and after apical instrumentation. Degree of canal curvature was also measured with Schneider's method in radiographs. Data of working length and canal curvature changes were statistically analyzed with one-way ANOVA and Tukey's studentized range test.

Working length and canal curvature were decreased significantly in each step in all instrumentation groups. Coronal flaring using Gates Glidden burs in hand instrument groups and whole canal instrumentation using stainless steel hand K-files caused significantly more working length change than in ProFile instrumentation group (p < 0.05).

The result of this study demonstrates that all of the above kinds of instrumentation in curved canals cause reduction of working length and canal curvature at each instrumentation steps, and hand instrumentation causes more working length change than ProFile.

The aims of the study were to evaluate the effect of epinephrine-containing local anesthetics on pulpal blood flow (PBF) and to investigate its effect on cavity preparation-induced PBF change. PBF was recorded using a laser Doppler flowmeter (Perimed Co., Sweden) from canines of nine cats under general anesthesia before and after injection of local anesthetics and after cavity preparation. 2% lidocaine hydrochloride with 1 : 100,000 epinephrine was administered by local infiltration given apical to the mandibular canine at the vestibular area and the same volume of isotonic saline was injected on the contralateral tooth as a control. A round carbide bur was operated at slow speed with isotonic saline flushing to grind spherical cavities with increasing depth through the enamel and into the dentin on both teeth. The obtained data was analyzed with paired t-test.

Cavity preparation caused significant increase of PBF (n = 9, p < 0.05). Local infiltration of lidocaine with epinephrine resulted in decreases of PBF (n = 9, p < 0.05), whereas there was no significant change of PBF with the physiologic saline as a control. Cavity preparation on tooth anesthetized with lidocaine with epinephrine caused significantly less increase of PBF than in control tooth (p < 0.05).

Therefore, the result of the present study demonstrates that local infiltration of 2% lidocaine with 1 : 100,000 epinephrine effectively reduces PBF increase caused by cavity preparation.