The aim of this study was to compare the cyclic fatigue resistance of the WaveOne Gold Glider, ProGlider and One G glide path instruments in artificial double-curvature canals.

This study included 15 WaveOne Gold Glider (size 15/0.08), 15 ProGlider (size 16/0.08), and 15 One G (size 16/0.06) nickel titanium files. The files were used in accordance with the manufacturer's instructions until they were broken in artificial double-curvature canals made of stainless steel. The time to fracture was recorded via a digital stopwatch and the number of rotations until fracture was also calculated. The data were statistically analyzed via the Kruskal-Wallis test.

The highest average number of rotations until fracture of the files was found for the WaveOne Gold Glider, followed by ProGlider and One G in order. Statistically significant differences were present between all groups of files (p < 0.05).

In our study, the resistance of the WaveOne Gold Glider nickel-titanium (Ni-Ti) file to cyclic fatigue in S-shaped curved canals was found to be higher than that of the ProGlider and One G Ni-Ti files.

The aim of this study was to investigate the effect of glide path preparation with PathFile and ProGlider nickel-titanium (NiTi) files on the cyclic fatigue resistance of WaveOne NiTi files.

Forty-four WaveOne Primary files were used and divided into four groups (n = 11). In the first group (0 WaveOne), the WaveOne Primary files served as a control group and were not used on acrylic blocks. In the 1 WaveOne Group, acrylic blocks were prepared using only WaveOne Primary files, and in the PF+WaveOne group and PG+WaveOne groups, acrylic blocks were first prepared with PathFile or ProGlider NiTi files, respectively, followed by the use of WaveOne Primary files. All the WaveOne Primary files were then subjected to cyclic fatigue testing. The number of cycles to failure was calculated and the data were statistically analyzed using one-way analysis of variance (ANOVA) and the Tukey honest significant difference multiple-comparison test at a 5% significance level.

The highest number of cycles to failure was found in the control group, and the lowest numbers were found in the 1 WaveOne group and the PF+WaveOne group. Significant differences were found among the 1 WaveOne, PF+WaveOne, and control groups (p < 0.05). No statistically significant differences were found between the PG+WaveOne group and the other three groups (p > 0.05).

Glide path preparation with NiTi rotary files did not affect the cyclic fatigue resistance of WaveOne Primary files used on acrylic blocks.

It was aimed to compare the cyclic fatigue resistances of ProGlider (PG), One G (OG), and HyFlex EDM (HEDM) nickel titanium glide path files in single- and double-curved artificial canals.

40 PG (16/0.02), 40 OG (14/0.03), and 40 HEDM (10/0.05) single-file glide path files were used in the present study. Sixty files were subjected to cyclic fatigue test by using double-curved canals and 60 files by using single-curved canal (n = 20). The number of cycles to fracture (NCF) was calculated and the length of the fractured fragment (FL) was determined by a digital micro-caliper. Twelve pieces of fractured files were examined with scanning electron microscope to determine fracture types of the files (n = 2). The NCF and the FL data were analyzed using one-way analysis of variance and post hoc Tukey test using SPSS 21 software (p < 0.05).

In all of the groups, NCF values were significantly lower in double-curved canals when compared to single-curved canals (p < 0.05). For both of single- and double-curved canals, NCF values of HEDM group in apical and coronal curvatures were found to be significantly higher than NCF values of PG and OG groups (p < 0.05). In both of single- and double-curved canals, NCF value of PG group was found significantly higher than OG group (p < 0.05).

Within the limitations of this study, HEDM glide path files were found to have the highest cyclic fatigue resistance in both of single- and double-curved canals.

The aim was to evaluate dentinal crack formation after root canal preparation with ProTaper Next system (PTN) with and without a glide path.

Forty-five mesial roots of mandibular first molars were selected. Fifteen teeth were left unprepared and served as controls. The experimental groups consist of mesiobuccal and mesiolingual root canals of remaining 30 teeth, which were divided into 2 groups (n = 15): Group PG/PTN, glide path was created with ProGlider (PG) and then canals were shaped with PTN system; Group PTN, glide path was not prepared and canals were shaped with PTN system only. All roots were sectioned perpendicular to the long axis at 1, 2, 3, 4, 6, and 8 mm from the apex, and the sections were observed under a stereomicroscope. The presence/absence of cracks was recorded. Data were analyzed with chi-square tests with Yates correction.

There were no significant differences in crack formation between the PTN with and without glide path preparation. The incidence of cracks observed in PG/PTN and PTN groups was 17.8% and 28.9%, respectively.

The creation of a glide path with ProGlider before ProTaper Next rotary system did not influence dentinal crack formation in root canals.