The purpose of this study was to compare the effect on marginal leakage of a resin surface sealant (Biscover) applied before or after polymerization of composite resin to unsealed composite restorations. Thirty Class V cavities with the occlusal margin in enamel and cervical margin in dentin or cementum were prepared on the buccal surfaces of sound extracted molars and restored with a microfilled light-cured composite resin (Micronew). Restorations were randomly assigned into one of three equal groups (n = 10): a control group - no surface sealing, group 1 - applied Biscover after polymerization of the composite resin, and group 2 - applied Biscover before polymerization of the composite resin. Specimens were thermocycled, immersed in a 2% methylene blue solution for 4 hours, sectioned longitudinally, and analyzed for leakage at the occlusal and gingival margins. The results of this study were as follows;

1. In sealed group, group 2 showed higher microleakage than group 1 at both occlusal and gingival margins, but there was no significant difference between two groups (p > 0.05).

2. Unsealed control group showed a little higher microleakage than sealed group at occlusal margins, and a little higher or similar microleakage than sealed group at gingival margins (p > 0.05).

3. Control group and group 2 showed significantly less microleakage at the occlusal margins, but group 1 showed no significantly difference between microleakage at the occlusal and gingival margins.

The purpose of this study was to evaluate the effect of immediate or delayed composite resin filling on dentinal microtensile bond strength (µTBS) after applied the adhesive.

The coronal dentin of human third molars was exposed. Single-Bond or One-Step was applied on the dentin surfaces, and composite resin were constructed immediately (group 1) or 5 min., 10 min., 15 min., 20 min. and 30 min. (groups 2-6) after an adhesive was applied. The specimens were sectioned and made bar-shaped. Each surface area of them was about 1mm². The µTBS test was performed by EZ test. The results were analysed by One-way ANOVA and Tukey's test at 95% significance level.

The results suggested that the µTBS of Single-Bond to dentin was decreased when the composite resin was constructed 20 min. and 30 min. after Single-Bond was applied. But the µTBS of One-Step was not affected by delayed composite resin filling.

This study evaluated the microleakage and interfacial gap between enamel and composite resin under the dry and wet condition of the enamel surface. V shaped class 5 cavities were prepared on the occlusal portion of extracted human molars. Samples were divided into three groups: D group (air dry for 10-15 s), BD group (blot dry with moist cotton pellet), and DR group (air dry for 10-15 s and rewet with Aqua-Prep F for 20 s).

Cavities were filled using Aelitefil composite resin after applied One-Step. Microleakage was tested by 2% methylene blue dye solution and the data were statistically analysed by Kruskal-Wallis test and Mann-Whitney test. Also Enamel-resin interface was observed under SEM. Group BD showed statistically lower microleakage than group D (p < 0.05), but there was no statistically significant difference between group BD and DR (p > 0.05). At the enamel-resin interface, group D showed the gap of 2 µm thickness, but group BD and DR showed close adaptation.

In conclusion, the use of blot dry and rewetting agent (Aqua-Prep F) resulted in decreased microleakage and improved adhesion between enamel and resin when using One-Step.

This study evaluated the marginal microleakage of five single step adhesives. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were prepared on both buccal and lingual surfaces of extracted human molar teeth. Prepared teeth were randomly divided into five groups and restored using one of the single step adhesives and composite resins: Prompt L-Pop/Filtek Z-250 (Group 1), AQ Bond/Metafil CX (Group 2), One-Up Bond F/Palfique Toughwell (Group 3), Futurabond/Admira (Group 4), Xeno III/Spectrum TPH (Group 5).

The restored teeth were thermocycled. Microleakage was assessed by dye penetration using 2% methylene blue dye solution. The teeth were bisected buccolingually and evaluated for microleakage under steromicroscope. The data were statistically analysed by Kruskal-Wallis test and Mann-Whitney tests.

The results of this study were as follows;

Microleakage of enamel margins in group 3 was statistically higher than that in groups 1, 2, 4, 5 (p < 0.05).

In conclusion, Prompt L-Pop showed the least leakage at enamel margin, and AQ Bond showed at dentin margin in this study. Marginal miroleakage in dentin was higher than that in enamel.

This study investigated that the effect of rewetting agent on dentinal microtensile bond strength (µTBS). Human molars were sectioned to expose the superficial dentin surfaces.

Samples were divided into two groups according to type of adhesives-Single Bond (S) and One-Step (O)], and again subdivided into five groups by different dentin surface treatment-dry for 15s (D), blot dry (BD) or dry for 15s, and rewet with different rewetting agents [distilled water (DW), Gluma Desensitizer (GD) and Aqua-Prep (AP)] for 30s. After application of adhesive, composite resin was built up on the bonding surface. Each tooth was sectioned to obtain stick with 1 mm² cross sectional area and the µTBS was determined by EZ test.

In the S group, the mean µTBS of GD, AP and BD group was significantly higher than that of DW and D group (p < 0.05). In the O group, the mean µTBS of AP, GD, BD and DW group was significantly higher than that of D group (p < 0.05).

The data suggested that Gluma Desensitizer and Aqua-Prep could be successfully used as rewetting agents, and Distilled water could be acceptable in aceton based adhesive system only.

This study evaluated the influence of application time of self-etching primers on microtensile bond strength (μTBS) to dentin using three self-etching primer adhesive systems.

Dentin surfaces were exposed from forty-eight human molars. They were conditioned with three self-etching primers (Clearfil SE Bond [SE], Unifil Bond [UF], Tyrian SPE + One Step Plus [TY]) and different primining times (10s, 20s, 30s and 40s). Composite resins were bonded to dentin surfaces and specimens were made. μTBS was tested and statistically compared using by one-way ANOVA and Tukey’s Test.

The results of this study presented that priming time for 10s in SE and UF groups and for 30s and 40s in TY group was highly decreased μTBS to dentin.