A variety files made of stainless steel (S-S) or nickel-titanium (Ni-Ti) are used during endodontic treatment. The purpose of this study was to evaluate the corrosion susceptibility of S-S and Ni-Ti endodontic files. Three brands of files were used for this study: K-flex® S-S files (Maillefer, USA), Profile® Ni-Ti files (Maillefer, USA), K-3® Ni-Ti files (SybronEndo, USA). 120 files of each brands (21mm, ISO size #20) were divided into 12 groups according to 1) sterilization methods using Autoclave or Ethylene Oxide (E-O) gas, 2) Irrigation solutions using 5.25 % NaOCl or Saline, 3) the number of sterilization (1, 5, 10 times). After above procedures, each of the files was inspected by three examiners with a light microscope and camera at X25. Each file was judged and ranked according to the following criteria: 0; no corrosion, 1; mild corrosion, 2; moderate corrosion, and 3; severe corrosion. The files of high score were examined under the Scanning Electron Microscope.

Data were statistically analyzed with the Kruskal-Wallis test (p < 0.05). Most of the ten time-autoclaved files had showed mild to moderate corrosion. But, one or five time-autoclaved files did not show corrosive surface. NaOCl treatment and E-O gas sterilization did not influence on corrosion. There was a significant difference in corrosion susceptibility between sterilization methods and the number of autoclaving. However, there was no significant difference between brands and file materials.

Citations

Citations to this article as recorded by  

• Comparison of Various Cold Sterilization Techniques on Routinely used Carbide Burs and Diamond Points
  Suganthi Ranganathan, Supriya Manvi, Srivatsa Gopalakrishna, Chaitra Koppal Renukanath
  International Journal of Prosthodontics and Restorative Dentistry.2017; 7(3): 97.     CrossRef