- Research Article The effect of thermocycling on the degree of conversion and mechanical properties of a microhybrid dental resin composite
-
Mehrsima Ghavami-Lahiji1,2
, Melika Firouzmanesh1, Hossein Bagheri3, Tahereh S. Jafarzadeh Kashi1,4, Fateme Razazpour1,2, Marjan Behroozibakhsh1,2 -
Restor Dent Endod 2018;43(2):e26.
DOI: https://doi.org/10.5395/rde.2018.43.e26
Published online: April 26, 2018
1Department of Dental Biomaterials, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran.
2Research Center for Science and Technology in Medicine, Tehran University of Medical Sciences, Tehran, Iran. JFIF d d Ducky d qhttp://ns.adobe.com/xap/1.0/ |er˭|I|-fGK.rΛp8XV1%K6mvG+tc+qE &ǸC_Nm:l=_/m5^[dߌڇ.c<%:)tQ$Ow~-aY;UJ >=F)2[nk؆?훐 M=l6[4(O.]2#-H^n#->&mp5~Fӛ+|| S,xag% qkEUzUgæBhߕP(7]kFnq?֖Cpru Z6*rEڊtS|*tI*E}7R<,nUU֫^I7Q*mSly%rdȓd8hE<9oHhMfNSRj[i7D[Rj݊+kდq{"$$H?p \̅S?㭻;t~ R߁ )^/>Qj`yt[w ԛ;² ~+ ߔ_ YW~|o] ?x^ᯛ `ʼn;g)T@vWn]>&4l p+$D̢1l|ȨF%-} .9[}w~
ԠLM9hСablfe&QoW !s ?wjLK?s7yO>(=C~_nyǜu? v 3vyo oI@qV-jeES^[9WoSܝh"l2C1a͔CiJ@3:Pճw= /7ovuk+\V;lDgն <[A+r X~d;m!_s8ݖ;;.0llUC+?i#_crʙ1~C.\q u l8Hܶ2m`ܻM3Tov|Bs rɵ"oLS-
DКw=Tv@f '6|YlD͓Y%-#Ѯo%:&!3o%\J<02;K87>^vgƓ# ;ݝmz^Y6=PS39U%~
&f#
}o!muH; ʲŇ˷yvP+&.7e[3'vR4Yj̗IZ`e˽3o[WU{
m[sUbۋZǾۆl6~9'V*.\S2<Sd*zY[aŶ`]C$n.v^Ʌ
dng>ەZ,Mmϑ :n6nϦezW qUJ4! ۇ4R! =>>F n|Q[{pRO 17ƕ~._I ''00k=b՛o}Osðc2'o\3}ݭQ^ 2 . R1yKȣtAݿ-u ܾw!`?1Whn|gzU o[ECWwjUIן)^h#1ɭ!/Z
np;o;ΗŻkXs."6E`Z1
עӐ9Kl8qd q} 2Stt;#j>;խabONŗ=fwP1j)l6J̶|gV 2`y/0E˛6+ԫ1?
6}KW c\KoKͨ2ۅFws*TԞLיuDx .kCzWXhy۶gLu|%TnupǺl-S* P RaLnT+c+*xl.v!.U=|; !_L̎뱚U=4hm:ٯ"y)$:>%(n}X'p[ȴ
^˒4kƓmzDx
\
'Nq amP7nyN݅=
3Dental Materials Research Center, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran. JFIF d d Ducky d qhttp://ns.adobe.com/xap/1.0/ |er˭|I|-fGK.rΛp8XV1%K6mvG+tc+qE &ǸC_Nm:l=_/m5^[dߌڇ.c<%:)tQ$Ow~-aY;UJ >=F)2[nk؆?훐 M=l6[4(O.]2#-H^n#->&mp5~Fӛ+|| S,xag% qkEUzUgæBhߕP(7]kFnq?֖Cpru Z6*rEڊtS|*tI*E}7R<,nUU֫^I7Q*mSly%rdȓd8hE<9oHhMfNSRj[i7D[Rj݊+kდq{"$$H?p \̅S?㭻;t~ R߁ )^/>Qj`yt[w ԛ;² ~+ ߔ_ YW~|o] ?x^ᯛ `ʼn;g)T@vWn]>&4l p+$D̢1l|ȨF%-} .9[}w~
ԠLM9hСablfe&QoW !s ?wjLK?s7yO>(=C~_nyǜu? v 3vyo oI@qV-jeES^[9WoSܝh"l2C1a͔CiJ@3:Pճw= /7ovuk+\V;lDgն <[A+r X~d;m!_s8ݖ;;.0llUC+?i#_crʙ1~C.\q u l8Hܶ2m`ܻM3Tov|Bs rɵ"oLS-
DКw=Tv@f '6|YlD͓Y%-#Ѯo%:&!3o%\J<02;K87>^vgƓ# ;ݝmz^Y6=PS39U%~
&f#
}o!muH; ʲŇ˷yvP+&.7e[3'vR4Yj̗IZ`e˽3o[WU{
m[sUbۋZǾۆl6~9'V*.\S2<Sd*zY[aŶ`]C$n.v^Ʌ
dng>ەZ,Mmϑ :n6nϦezW qUJ4! ۇ4R! =>>F n|Q[{pRO 17ƕ~._I ''00k=b՛o}Osðc2'o\3}ݭQ^ 2 . R1yKȣtAݿ-u ܾw!`?1Whn|gzU o[ECWwjUIן)^h#1ɭ!/Z
np;o;ΗŻkXs."6E`Z1
עӐ9Kl8qd q} 2Stt;#j>;խabONŗ=fwP1j)l6J̶|gV 2`y/0E˛6+ԫ1?
6}KW c\KoKͨ2ۅFws*TԞLיuDx .kCzWXhy۶gLu|%TnupǺl-S* P RaLnT+c+*xl.v!.U=|; !_L̎뱚U=4hm:ٯ"y)$:>%(n}X'p[ȴ
^˒4kƓmzDx
\
'Nq amP7nyN݅=
4Iranian Tissue Bank and Research Center, Tehran University of Medical Sciences, Tehran, Iran. JFIF d d Ducky d qhttp://ns.adobe.com/xap/1.0/ |er˭|I|-fGK.rΛp8XV1%K6mvG+tc+qE &ǸC_Nm:l=_/m5^[dߌڇ.c<%:)tQ$Ow~-aY;UJ >=F)2[nk؆?훐 M=l6[4(O.]2#-H^n#->&mp5~Fӛ+|| S,xag% qkEUzUgæBhߕP(7]kFnq?֖Cpru Z6*rEڊtS|*tI*E}7R<,nUU֫^I7Q*mSly%rdȓd8hE<9oHhMfNSRj[i7D[Rj݊+kდq{"$$H?p \̅S?㭻;t~ R߁ )^/>Qj`yt[w ԛ;² ~+ ߔ_ YW~|o] ?x^ᯛ `ʼn;g)T@vWn]>&4l p+$D̢1l|ȨF%-} .9[}w~
ԠLM9hСablfe&QoW !s ?wjLK?s7yO>(=C~_nyǜu? v 3vyo oI@qV-jeES^[9WoSܝh"l2C1a͔CiJ@3:Pճw= /7ovuk+\V;lDgն <[A+r X~d;m!_s8ݖ;;.0llUC+?i#_crʙ1~C.\q u l8Hܶ2m`ܻM3Tov|Bs rɵ"oLS-
DКw=Tv@f '6|YlD͓Y%-#Ѯo%:&!3o%\J<02;K87>^vgƓ# ;ݝmz^Y6=PS39U%~
&f#
}o!muH; ʲŇ˷yvP+&.7e[3'vR4Yj̗IZ`e˽3o[WU{
m[sUbۋZǾۆl6~9'V*.\S2<Sd*zY[aŶ`]C$n.v^Ʌ
dng>ەZ,Mmϑ :n6nϦezW qUJ4! ۇ4R! =>>F n|Q[{pRO 17ƕ~._I ''00k=b՛o}Osðc2'o\3}ݭQ^ 2 . R1yKȣtAݿ-u ܾw!`?1Whn|gzU o[ECWwjUIן)^h#1ɭ!/Z
np;o;ΗŻkXs."6E`Z1
עӐ9Kl8qd q} 2Stt;#j>;խabONŗ=fwP1j)l6J̶|gV 2`y/0E˛6+ԫ1?
6}KW c\KoKͨ2ۅFws*TԞLיuDx .kCzWXhy۶gLu|%TnupǺl-S* P RaLnT+c+*xl.v!.U=|; !_L̎뱚U=4hm:ٯ"y)$:>%(n}X'p[ȴ
^˒4kƓmzDx
\
'Nq amP7nyN݅=
- Correspondence to Mehrsima Ghavami-Lahiji, DDS. PhD Candidate, Department of Dental Biomaterials, School of Dentistry, Tehran University of Medical Sciences, North Kargar Avenue, Tehran 14174, Iran. dr.m.ghavami@gmail.com
• Received: December 11, 2017 • Accepted: March 19, 2018
Copyright © 2018. The Korean Academy of Conservative Dentistry
This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (https://creativecommons.org/licenses/by-nc/4.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
- 7,523 Views
- 67 Download
- 88 Crossref
Abstract
-
Objective The purpose of this study was to investigate the degree of conversion (DC) and mechanical properties of a microhybrid Filtek Z250 (3M ESPE) resin composite after aging.
-
Method The specimens were fabricated using circular molds to investigate Vickers microhardness (Vickers hardness number [VHN]) and DC, and were prepared according to ISO 4049 for flexural strength testing. The initial DC (%) of discs was recorded using attenuated total reflectance-Fourier transforming infrared spectroscopy. The initial VHN of the specimens was measured using a microhardness tester under a load of 300 g for 15 seconds and the flexural strength test was carried out with a universal testing machine (crosshead speed, 0.5 mm/min). The specimens were then subjected to thermocycling in 5°C and 55°C water baths. Properties were assessed after 1,000–10,000 cycles of thermocycling. The surfaces were evaluated using scanning electron microscopy (SEM). Data were analyzed using 1-way analysis of variance followed by the Tukey honest significant difference post hoc test.
-
Results Statistical analysis showed that DC tended to increase up to 4,000 cycles, with no significant changes. VHN and flexural strength values significantly decreased upon thermal cycling when compared to baseline (p < 0.05). However, there was no significant difference between initial and post-thermocycling VHN results at 1,000 cycles. SEM images after aging showed deteriorative changes in the resin composite surfaces.
-
Conclusions The Z250 microhybrid resin composite showed reduced surface microhardness and flexural strength and increased DC after thermocycling.
INTRODUCTION
Today, resin composites are widely used to build up anterior and posterior dental restorations due to their improved physical-mechanical properties and increasing aesthetic demands [1]. Resin composites comprise a polymeric matrix, filler particles, and a silane coupling agent that links the matrix to the fillers, as well as minor additional components including initiators, stabilizers, and coloring pigments. As with other composite structures, the type and composition of the resin matrix and the filler particles influence the mechanical properties of these materials, which eventually determine their clinical performance. Resin composite restorations are subjected to temperature variations in the oral cavity induced by diet and to complex chewing forces with a considerable amount of flexural stresses [1,2].
When a polymer-based material such as resin is applied in the oral environment, it may incompletely withstand degradation [3,4]. As a result, there may be a decrease in its functional properties, such as flexural strength and hardness. Different periods of water storage and thermocycling are among the several methods used to simulate the aging process of dental materials in in vitro studies. These methods attempt to simulate the hydrolytic degradation that occurs in resin-based composite (RBC) restorations in service [5]. Many studies have investigated the mechanical properties and degree of conversion (DC) of dental resin composites [6,7,8,9]. Dental resin composites used for coronal reconstruction are exposed to moisture and temperature variations. Few of these studies, however, have analyzed the behavior of aged materials. Indeed, the effect of thermocycling on composites can be more detrimental than that of water alone, because of increased degradation of the polymeric network by hydrothermal aging [10].
It has been found that the degree of monomer conversion in resin composites greatly affects the physical properties of these restorative materials. The DC can be defined as the percentage of reacted carbon-carbon double (C=C) bonds, and can affect many properties of the resin materials, including mechanical properties, dimensional stability, solubility, biocompatibility, and stain susceptibility. The unreacted double bonds may be found either in free monomers or in pendant groups existing on the network. The unreacted monomer may leach from the polymerized dental composites and affect the soft tissues [11]. The functional performance of a dental resin composite depends on its mechanical, chemical, and biological properties. These properties are related to the polymer network and polymerization parameters, such as the rate of polymerization and DC. However, few studies have examined the DC of aged composites [2,9,12]. Among the various methods used to determine the DC of resin composites, Fourier transform infrared spectroscopy (FTIR) has been proven to be an effective and reliable tool that works by detecting stretching vibrations of C=C bonds before and after the curing of materials [13].
Resin composite restorations are exposed to complex chewing forces with a considerable amount of flexural stresses in the oral environment. The flexural strength of a material is the maximum stress that it can resist before failure when subjected to a bending load. The clinical applications determine how much flexural strength is required. For restorations under strong chewing forces, high flexural strength is clearly desired [14]. Although some published studies have investigated the behavior of aged composite in regard to its ability to bond with new composite or resin luting cement, there is little information in the literature on the physical and mechanical behavior of aged composite itself, such as the DC, microhardness, and flexural strength and how such parameters are related to different degrees of aging.
The objective of this study was to evaluate the effect of thermocycling on the DC, flexural strength, and microhardness of a dental resin composite. Thus, the null hypothesis tested was that thermocycling would not affect the DC, microhardness, and flexural strength of the dental resin composite.
MATERIALS AND METHODS
The dental resin composite used in this study was a microhybrid Filtek Z250 (Shade A1, 3M ESPE, St. Paul, MN, USA). The composition of the material is shown in Table 1.
Table 1
Composition of organic matrix and filler of Filtek Z250 microhybrid universal dental composite
The specimen disks of the dental composite for determining the DC were prepared using a polyethylene mold (7 mm in diameter and 1 mm in height). A small Mylar strip with a thickness of 0.7 mm was placed on a glass slab. The mold was placed on the strip and, after filling the mold to excess, the surface of the material was covered with another Mylar strip and a glass slide, and a weight of 500 g was placed on it for 20 seconds to ensure better accommodation of the resin composite and to remove the excess material. All the composite specimens (n = 5) were light-activated with an LED curing unit (Woodpecker WM-199, Foshan Vimel Dental Equipment Co., Ltd., Guangdong, China) with a light intensity of 500 mW/cm2 and a tip diameter of 7 mm for 20 seconds on both the top and bottom sides. Specimens were then stored in distilled water at 37°C for 24 hours to ensure polymerization. After 24 hours, the specimens were removed from the molds. The specimens were placed in a basket and alternated between 5°C and 55°C water baths with a dwell time of 20 seconds and a rest time of 20 seconds (Dorsa apparatus, Tehran, Iran).
The DC was measured in the polymerized specimens. The initial DC (%) of the discs was recorded after 24 hours of storage in distilled water in the absorbance mode using attenuated total reflectance-Fourier transforming infrared spectroscopy (ATR-FTIR; NICOLET iS10, Thermo Fisher Scientific, Waltham, MA, USA) with a Smart OMNI-Transmission accessory. Subsequent measurements of the DC of the thermocycled specimens were made after aging. The DC was measured 7 times in this study: after 24 hours of storage in distilled water, and then after 1,000, 2,000, 4,000, 6,000, 8,000, and 10,000 cycles. Specimens were marked to be examined for DC after the corresponding number of cycles.
The absorption spectra of the cured and uncured composites were obtained at the top surfaces in the region of 400–4,000 cm−1 wavelength using 4 scans at a resolution of 16 cm−1. The range from 1,590 to 1,660 cm−1 was then expanded (Figure 1). The percentage of unreacted C=C bonds (%) for the methacrylate-based composite was calculated from the ratio of the absorbance peak area of aliphatic C=C bonds (1,638 cm−1 wavelength) against an internal standard (aromatic C=C, 1,608 cm−1 wavelength) before and after curing of the specimen using Omnic software. The DC was then calculated by subtracting the percentage of the C=C bonds from 100%, according to the following equation.
Figure 1
Fourier transform infrared spectroscopy (FTIR) spectra of the resin composites before (upper red) and after setting (lower green).
The mean values of DC after a certain number of thermocycles were compared using 1-way analysis of variance (ANOVA). The Tukey honest significant difference (HSD) test was used for pair-wise comparisons. All statistical analyses were performed at a significance level of α = 0.05.
The specimens were fabricated using circular polyethylene molds (7 mm in diameter and 1 mm in width) for the Vickers microhardness test. Specimens were light cured with an LED curing unit and stored in a water bath at 37°C for 24 hours. Then, the specimens were randomly divided into 4 groups (n = 10). The surface microhardness of the specimens was measured using a microhardness tester (Baresiss, Oberdischingen, Germany) under a load of 300 g for 15 seconds for 10 specimens (G1). The average value of the 3 indentations for each specimen was taken as the Vickers hardness number (VHN). The remaining specimens were subjected to thermocycling using 5°C and 55°C water baths, with a dwell time of 20 seconds. Microhardness was assessed again after 1,000, 4,000, and 10,000 cycles (G2–G4). Data were analyzed using 1-way ANOVA and the Tukey HSD post hoc test.
For the flexural strength test, a stainless-steel mold (25 × 2 × 2 mm) was utilized to prepare the specimens according to ISO 4049. The mold was placed on a glass slide over a Mylar sheet. Light-cured resin composite was condensed into the mold, and a Mylar sheet and another glass slide were placed over them. The assembly was placed under a clamp and adequate pressure was applied. The middle third of the specimen was first cured for 20 seconds with a 650 mW/cm2 LED, and then the remaining thirds were cured in the same manner as the middle third by overlapping with the central part. The same procedure was applied to the lower surface of the specimen. After irradiation, the assembly was placed into a water bath at 37°C for 15 minutes. The flash was then removed with the use of sandpaper, and the test specimens were separated from their molds and again stored in a water bath at 37°C for 24 hours.
Twenty-four hours after irradiation, the specimens were randomly divided into 4 groups (n = 10). Flexural strength testing was then carried out with a universal testing machine (Santam 20, Santam Design & Manufacturing Company, Tehran, Iran) with a load cell of 6 kg (Bongshin, Seongnam, Korea) at a crosshead speed of 0.5 mm/min until the specimen was fractured. The maximum load exerted on the specimen was recorded, and flexural strength (in MPa) was calculated with the following equation.
The same procedures were followed after 1,000, 4,000, and 10,000 cycles. Data were analyzed using 1-way ANOVA and the Tukey HSD post hoc test.
In order to investigate the effect of thermocycling on the surface degradation of resin composites, 2 specimen discs were analyzed by SEM. The discs were dried, sputter-coated, and observed using SEM (TESCAN, VEGA, Brno, Czech Republic). The SEM images were taken at ×2,000, ×5,000, and ×15,000 magnifications.
RESULTS
The FTIR spectra of the resin composites before and after curing are shown in Figure 1. Table 2 shows the DC values that were obtained and the results of their multiple comparisons for aged composites. The DC calculated using the above formula was 61.01% ± 3.69% at the baseline. The DC increased up to 4,000 cycles (68.03% ± 4.64%), and did not significantly change thereafter. The Tukey HSD post hoc test showed no significant differences between 1,000 or 2,000 intervals of thermal cycling for the aged composite (p > 0.05). However, thermocycling after 4,000 cycles significantly increased the DC compared to the baseline (p < 0.05). Further thermocycling from 4,000 to 10,000 cycles did not significantly alter the DC. On FTIR spectroscopy, the band in the range of 3,100–3,700 cm−1 tended to broaden with increasing thermocycling (Figure 2).
Table 2
Degree of conversion (DC, %) of the thermocycled specimens
Figure 2
Fourier transform infrared spectroscopy (FTIR) spectra of the resin composites after thermocycling. (A) After 10,000 cycles; (B) After 4,000 cycles; (C) After 1,000 cycles; (D) Baseline after curing.
Thermocycling tended to reduce the flexural strength (G1 to G4). One-way ANOVA showed statistically significant differences during aging (p < 0.05). Thermocycling had a significant effect on flexural strength. The Tukey HSD post hoc test was used for pair-wise comparison of means. There were significant changes among the groups (p < 0.05, Table 3).
Table 3
Flexural strength (FS) and microhardness of the thermocycled specimens
Values of FS and microhardness are presented as means ± standard deviations. Values marked with different lower-case superscript letters are significantly different (Tukey HSD post hoc test, p < 0.05).
CV, coefficient of variation; VHN, Vickers hardness number; G1, group 1; G2, group 2; G3, group 3; G4, group 4; HSD, honest significant difference.
The analysis revealed statistically significant differences in the mean hardness values for the different aging times. The VHN values of the resin composite significantly decreased upon thermal cycling when compared to the baseline (G1) (p < 0.05). However, there was no significant difference between G1 and G2. Thermocycling up to 10,000 times (G4) produced the lowest VHN values among the groups, and this tendency was statistically significant (61.05 ± 3.06 kgf/mm2, Table 3).
Comparison of the coefficient of variation (CV, %) of mean values for the DC showed greater variation at 4,000 and 6,000 cycles, which decreased at the end of the experiment. The highest DC values were observed at 6,000 cycles with a relatively low CV. VHN values showed a higher CV for 4,000 cycles, whereas in the flexural strength test, more variation was present at 1,000 cycles. The DC values demonstrated less variation than the other 2 tests (flexural strength and microhardness). Moreover, the SEM analysis showed noticeable superficial changes attributable to thermocycling in the resin composites.
DISCUSSION
Aging of RBCs is often the outcome of mechanical mechanisms of physical degradation such as wear, abrasion, and fatigue. It may also be due to mechanisms of chemical degradation such as temperature-related breakdown or enzymatic, hydrolytic, and acidic processes. Exposing the specimens to thermocycling regimens is a common technique for simulating hydrothermal aging [5,15]. Alternating temperatures between 5°C and 55°C, coupled with the presence of water, contributed to the aging of RBC in this study. Our objective was to investigate artificial aging-induced changes in microhybrid dental composites. Specimens were subjected to thermal aging ranging from 1,000 to 10,000 cycles in the DC test. According to ISO 11405, the use of 500 thermal cycles between 5°C and 55°C is considered to be suitable to simulate short-term aging of dental materials [16]. In addition, Gale and Darvell [17] proposed that 10,000 cycles might represent approximately 1 year of in vivo functioning, with 20 to 50 cycles considered equivalent to a single day. Therefore, we decided to continue thermal cycling to 10,000 cycles to examine the results.
ATR-FTIR was employed in the absorbance mode in this study to determine the DC of the dental resin composite. This method is reliable and is not time-consuming. This technique is non-destructive, requires no sample preparation, and does not involve pulverization. Consequently, we were able to measure the DC at different times without losing the samples. The DC measurements increased up to 4,000 cycles. These findings are in accordance with the study of Pallikari and Iosifidou [12], who reported further advances in the DC of resin composites after artificial aging. However, in the aforementioned study, the aging of the samples was performed in 2 steps — initially by thermocycling and then by UV irradiation — and corresponded to 5 years of natural aging [12]. In a study conducted by Tonetto et al. [8], the DC of resin cements was investigated at 24-hour intervals until 7 days after light curing in the dry state in a dark room. They found the greatest DC at 7 days after curing, with completion of the polymerization reaction [8].
There are 2 possible explanations for why the DC increases over time. First, the elution of unreacted monomers caused by the release of monomers from the dental resin composite increases with thermal shocks and storage time [18]. Our study showed that the storage of specimens in water without thermal cycling did not have a considerable effect on DC. Therefore, it can be concluded that the increased temperature during thermal cycling may accelerate monomer dilution by increasing monomer diffusion. Sideridou and Achilias [19] detected leached monomers of this composite (Filtek Z250) using high-performance liquid chromatography. More of the monomer urethane dimethacrylate leached than other monomers, although a small amount of triethylene glycol dimethacrylate (TEGDMA) was detected. TEGDMA, which is a hydrophilic monomer, has been found to be released faster than other monomers [19]. In fact, several factors affect the leaching of monomers, including the type of monomers and fillers, the chemical structure of the resin, the resin/filler proportion, the type of the curing unit, and the elution medium [18]. Durner et al. [20] measured the DC and the amount of elutable substances from resin composites as a function of polymerization time (5–40 seconds). They observed a significant increase in DC as the polymerization time increased from 5 to 40 seconds, whereas the amount of elutable substances decreased, except for methacrylic acid [20].
The second reason may be continuation of the polymerization reaction of entrapped unreacted monomers. According to Andrzejewska [21], some free radicals entrapped in the polymer during the vitrification stage of dental resin composites may remain in the network for several weeks after vitrification [21,22]. Studies suggest that increasing temperature or swelling by the solvent or diffusion reaction can increase the mobility of the system, making such radicals able to react with any remaining double bonds within the network and continue the polymerization process [23]. In addition to free radicals, there are other ‘trapped’ active components in the polymer network, such as free monomers, pendant double bonds, and photoinitiators [24]. It has been reported that heating of the composite resin to a temperature of 55°C (close to the glass transition temperature [Tg]) is probably the driving force for continuing the polymerization. According to Truffier-Boutry et al. [25], the Tg of an organic matrix such as composite resin is close to 55°C. Storing the specimens at high temperatures close to the Tg could enhance the molecular mobility in the polymer matrix, causing radical recombination to occur. At temperatures below the Tg, the molecular mobility is low because the network is in a vitrified state [25]. Moreover, increasing the temperature may promote a diffusion reaction, so that small molecules can diffuse into the polymer matrix and encourage radical termination [22].
In this study, the DC of C=C double bonds in our composite was 60% ± 3.3% at the baseline, suggesting that approximately 40% of the C=C double bonds were ‘uncured.’ Leaching of uncured monomer, as mentioned before, may decrease the ratio of aliphatic to aromatic C=C bonds in the aged state compared with the cured state at the baseline. Subtracting this diminished proportion of C=C double bonds from 100%, according to the formula, may increase the amount of DC, which is in agreement with what we observed in our study. The spectra taken within the period of the experiment exhibited similar peaks/bands. However, the changes in C=C related peak areas indicated an enhanced DC. Furthermore, on FTIR spectra, the band in the 3,100–3,700 cm−1 range tended to be stronger with increasing aging time. This strong band can be interpreted as the O-H stretching band derived from increasing amounts of absorbed water over time.
ISO 4049 proposed a 3-point bending method for evaluating flexural strength [26]. Furthermore, in most articles, 3-point bending has been employed for the assessment of dental resin composites. Accordingly, we chose this method to allow a good comparison with previous studies. The measured values of flexural strength (117.04 ± 21.72 MPa) obtained from the microhybrid dental composite tested in this study without thermocycling was similar to those observed in other studies of Z250 composites. Attar et al. [27] found that the flexural strength was 117.4 ± 19.2 MPa at 24 hours and 95.6 ± 10.6 MPa after 1 month, and Chung et al. [6] found values ranging from 66.61 to 147.21 MPa after 1 week of storage in water. In fact, composite resins have a brittle nature and with increased aging time, they become more brittle, as shown by the superficial changes, degradation of the resin matrix, and debonding of fillers, which are clearly observed on SEM. Thus, we observed a significant decrease in flexural strength values after thermocycling, in good agreement with the findings reported by Souza et al. [2] and Janda et al. [28]. Therefore, the null hypothesis that thermal aging has no effect on the flexural strength of RBCs should be rejected. High or elevated temperatures are also known to weaken the resin-based materials. A minimum flexural strength of 80 MPa is considered appropriate by the ISO for restorative materials involving outer occlusal surfaces [26]. The results of the present study of up to 1,000 hydrothermal cycles exceeded the value required by ISO 4049 (80 MPa), but the flexural strength values after 4,000 cycles were below 80 MPa, and thus did not meet the limits of ISO 4049 for use as occlusal fillings.
The SEM micrographs produced at the end of the experiments in this study revealed superficial deterioration and a softer surface (Figure 3). Thus, we expected lower hardness values. With regard to the obtained microhardness results, there was a decreasing trend with continuing the thermal cycling of the specimens. In agreement with our study, de Moraes et al. [29] presented a significant decrease in hardness values and softer surfaces of a Z250 composite after 6 months of storage in water. For the subsurface, a decrease in hardness values after 1 year was reported [29]. Studies such as those conducted by Pereira et al. [30], and Souza et al. [2] in indirect resin composites (IRCs) have investigated the effect of thermocycling on microhardness. Pereira et al. [30] reported a significant decrease in microhardness values of 2 tested materials after 3,000 cycles of thermal cycling. However, Souza et al. [2] found that 5,000 thermal cycles did not decrease the microhardness of most IRCs. de Oliveira et al. [15] reported that the hardness of the microhybrid resin composite (Opallis) did not change either after storage in water or after thermocycling. It has been reported that polymeric chains with a high crosslinking density showed less water absorption due to the reduction of the free space. Moreover, in materials with a denser polymer network, less water absorption is expected [15]. Ferracane and Condon [31] reported a rapid elution of unreacted molecules and much slower water sorption after soaking of resin composites in water, in a process controlled by diffusion into the polymer matrix. During this gradual water sorption, water molecules tend to occupy the free volume between the cross-linked chains and micro-voids created during polymerization [32]. Slow water uptake of resin composite corresponds to the results of our study, in which significant alterations were found after 4,000 cycles in all 3 tests.
Figure 3
Scanning electron microscopy (SEM) micrograph of the Filtek Z250 resin composite at ×15,000 magnification. (A) Freshly cured material; (B) After 10,000 cycles of thermocycling; (C) After 14,000 cycles of thermocycling. Coarse protruding filler particles were present in the weakened resin matrix at the thermocycled resin composite surface. Some areas from which filler particles seem to have been debonded and plucked out were observed. The composite showed exposed particles and loosening of filler particles after aging.
The analysis of SEM images after aging has revealed deterioration in RBC surfaces. Hydrolytic degradation, as discussed above, can be explained by the fact that some electropositive ions that exist in filler particles tend to react with water, changing the internal charge balance of the silica matrix. By increasing the number of hydrogen ions that occupy the free spaces, the (Si-O-Si) bonds of the silica matrix break, and surface degradation and superficial softening thus occur with aging [3]. Prolonged thermal cycling can lead to water absorption and swelling of the matrix. Water sorption is considered a diffusion-controlled process in composite resins. The water taken up by the polymer network could result in filler-matrix debonding, softening of resins, and even the hydrolytic degradation of fillers. This could affect the mechanical properties of resin composites. In fact, the role of water is like a plasticizer that could weaken the polymer network. It can directly degrade the matrix-filler interface by causing the breakdown of chemical bonds of the silane-filler interface and filler particle surfaces. Unfortunately, the minimal number of thermal cycles required for complete plasticization is not known [2,4].
It seems that with the leaching of unreacted monomers over time, the findings become more homogeneous and show less variation. The observation of a smaller standard deviation and CV in specimens at the end of thermocycling protocol, particularly in the DC test, shows the higher predictability of the DC data in samples subjected to aging.
Although this study was conducted to simulate aging by thermocycling, resin composite materials in clinical situations are also subjected to the effects of beverages, food, mouthwashes, saliva (pH, composition, etc.), and the mechanical actions of chewing and brushing. Thus, these factors should be considered in future research. The performance of dental resin composites in clinically realistic circumstances needs further investigation. Despite the deteriorative changes that occurred in the current study, such considerations should be taken into account for composites subjected to aging. Due to financial limitations and the large amount of material used for tests in this study, only one material was tested. Within the limitations of this study, we evaluated a microhybrid resin composite to gain initial insights into the properties of this material. The mechanical properties and DC of other types of resin composites remain to be investigated in future studies.
CONCLUSIONS
Within the limitations of our in vitro study, it can be concluded that thermocycling increased the DC of the tested material significantly after 4,000 thermal cycling events compared to the baseline. Thermocycling also significantly decreased the hardness and the flexural strength of the tested material. The Z250 composite resin showed the lowest hardness and flexural strength values at the end of the experiment (after 10,000 thermal cycling events).
ACKNOWLEDGEMENT
The authors would like to thank the Research Center for Science and Technology in Medicine, Tehran University of Medical Sciences, Tehran, Iran.
-
Conflict of Interest: No potential conflict of interest relevant to this article was reported.
-
Author Contributions:
Conceptualization: Bagheri H, Jafarzadeh Kashi TS.
Data curation: Ghavami-Lahiji M, Firouzmanesh M, Razazpour F.
Formal analysis: Bagheri H, Jafarzadeh Kashi TS.
Funding acquisition: Firouzmanesh M.
Investigation: Ghavami-Lahiji M, Firouzmanesh M, Razazpour F.
Methodology: Ghavami-Lahiji M, Razazpour F.
Project administration: Ghavami-Lahiji M, Bagheri H, Jafarzadeh Kashi TS, Behroozibakhsh M.
Supervision: Bagheri H.
Validation: Jafarzadeh Kashi TS.
Writing - original draft: Ghavami-Lahiji M.
Writing - review & editing: Ghavami-Lahiji M, Jafarzadeh Kashi TS, Behroozibakhsh M.
- 1. Anusavice KJ, Phillips RW, Shen C, Rawls HR. Phillips' science of dental materials. 12th ed. St. Louis, Mo: Elsevier/Saunders; 2013.
- 2. Souza RO, Özcan M, Michida SM, de Melo RM, Pavanelli CA, Bottino MA, Soares LE, Martin AA. Conversion degree of indirect resin composites and effect of thermocycling on their physical properties. J Prosthodont 2010;19:218-225.ArticlePubMed
- 3. Martos J, Osinaga PW, Oliveira E, Castro LA. Hydrolytic degradation of composite resins: effects on the microhardness. Mater Res 2003;6:599-604.Article
- 4. Toledano M, Osorio R, Osorio E, Fuentes V, Prati C, Garcia-Godoy F. Sorption and solubility of resin-based restorative dental materials. J Dent 2003;31:43-50.ArticlePubMed
- 5. Özcan M, Corazza PH, Marocho SM, Barbosa SH, Bottino MA. Repair bond strength of microhybrid, nanohybrid and nanofilled resin composites: effect of substrate resin type, surface conditioning and ageing. Clin Oral Investig 2013;17:1751-1758.ArticlePubMedPDF
- 6. Chung SM, Yap AU, Chandra SP, Lim CT. Flexural strength of dental composite restoratives: comparison of biaxial and three-point bending test. J Biomed Mater Res B Appl Biomater 2004;71:278-283.ArticlePubMed
- 7. Obici AC, Sinhoreti MA, Frollini E, Sobrinho LC, Consani S. Degree of conversion of Z250 composite determined by fourier transform infrared spectroscopy: comparison of techniques, storage periods and photo-activation methods. Mater Res 2004;7:605-610.Article
- 8. Tonetto MR, Pinto SC, Rastelli Ade N, Borges AH, Saad JR, Pedro FL, de Andrade MF, Bandéca MC. Degree of conversion of polymer-matrix composite assessed by FTIR analysis. J Contemp Dent Pract 2013;14:76-79.ArticlePubMed
- 9. Jafarzadeh TS, Erfan M, Behroozibakhsh M, Fatemi M, Masaeli R, Rezaei Y, Bagheri H, Erfan Y. Evaluation of polymerization efficacy in composite resins via FT-IR spectroscopy and vickers microhardness test. J Dent Res Dent Clin Dent Prospect 2015;9:226-232.ArticlePubMedPMC
- 10. Gonçalves L, Filho JD, Guimarães JG, Poskus LT, Silva EM. Solubility, salivary sorption and degree of conversion of dimethacrylate-based polymeric matrixes. J Biomed Mater Res B Appl Biomater 2008;85:320-325.PubMed
- 11. Tosun G, Ozturk N, Sener Y, Gunduz B. Effect of light curing units and storage time on the degree of conversion of fissure sealants. Rev Clín Pesqui Odontol 2009;5:111-119.
- 12. Pallikari F, Iosifidou S. A study of aging in dental composites using IR and Raman spectroscopy. e-Polymer 2004;4:793-802.Article
- 13. Moraes LG, Rocha RS, Menegazzo LM, de Araújo EB, Yukimito K, Moraes JC. Infrared spectroscopy: a tool for determination of the degree of conversion in dental composites. J Appl Oral Sci 2008;16:145-149.ArticlePubMedPMC
- 14. McCabe JF, Walls AW. Applied dental materials. Hoboken, NJ: John Wiley & Sons; 2013.
- 15. de Oliveira JC, Aiello G, Mendes B, Urban VM, Campanha NH, Jorge JH. Effect of storage in water and thermocycling on hardness and roughness of resin materials for temporary restorations. Mater Res 2010;13:355-359.Article
- 16. International Organization for Standardization. ISO/TS 11405 Dentistry -- Testing of adhesion to tooth structure. 3rd ed. Geneva: International Organization for Standardization; 2015.
- 17. Gale MS, Darvell BW. Thermal cycling procedures for laboratory testing of dental restorations. J Dent 1999;27:89-99.ArticlePubMed
- 18. Tabatabaei MH, Sadrai S, Bassir SH, Veisy N, Dehghan S. Effect of food stimulated liquids and thermocycling on the monomer elution from a nanofilled composite. Open Dent J 2013;7:62-67.ArticlePubMedPMCPDF
- 19. Sideridou ID, Achilias DS. Elution study of unreacted Bis‐GMA, TEGDMA, UDMA, and Bis‐EMA from light‐cured dental resins and resin composites using HPLC. J Biomed Mater Res B Appl Biomater 2005;74:617-626.ArticlePubMed
- 20. Durner J, Obermaier J, Draenert M, Ilie N. Correlation of the degree of conversion with the amount of elutable substances in nano-hybrid dental composites. Dent Mater 2012;28:1146-1153.ArticlePubMed
- 21. Andrzejewska E. Photopolymerization kinetics of multifunctional monomers. Prog Polym Sci 2001;26:605-665.Article
- 22. Leprince J, Lamblin G, Truffier-Boutry D, Demoustier-Champagne S, Devaux J, Mestdagh M, Leloup G. Kinetic study of free radicals trapped in dental resins stored in different environments. Acta Biomater 2009;5:2518-2524.ArticlePubMed
- 23. Leprince JG, Lamblin G, Devaux J, Dewaele M, Mestdagh M, Palin WM, Gallez B, Leloup G. Irradiation modes' impact on radical entrapment in photoactive resins. J Dent Res 2010;89:1494-1498.ArticlePubMedPDF
- 24. Leprince JG, Palin WM, Hadis MA, Devaux J, Leloup G. Progress in dimethacrylate-based dental composite technology and curing efficiency. Dent Mater 2013;29:139-156.ArticlePubMed
- 25. Truffier-Boutry D, Demoustier-Champagne S, Devaux J, Biebuyck JJ, Mestdagh M, Larbanois P, Leloup G. A physico-chemical explanation of the post-polymerization shrinkage in dental resins. Dent Mater 2006;22:405-412.ArticlePubMed
- 26. International Organization for Standardization. ISO 4049 Dentistry -- Polymer-based restorative materials. 4th ed. Geneva: International Organization for Standardization; 2015.
- 27. Attar N, Tam LE, McComb D. Flow, strength, stiffness and radiopacity of flowable resin composites. J Can Dent Assoc 2003;69:516-521.PubMed
- 28. Janda R, Roulet JF, Latta M. The effects of thermocycling on the flexural strength and flexural modulus of modern resin-based filling materials. Dent Mater 2006;22:1103-1108.ArticlePubMed
- 29. de Moraes RR, Marimon JL, Schneider LF, Brandt WC, Correr Sobrinho L, Bueno M. Hydrolytic stability of dental composites: one-year aging effect on surface roughness and surface/subsurface hardness. Rev Odontol UNESP 2007;36:383-387.
- 30. Pereira SM, Castilho AA, Salazar-Marocho SM, Oliveira KM, Váquez VZ, Bottino MA. Thermocycling effect on microhardness of laboratory composite resins. Braz J Oral Sci 2007;6:1372-1375.
- 31. Ferracane JL, Condon JR. Rate of elution of leachable components from composite. Dent Mater 1990;6:282-287.ArticlePubMed
- 32. Ferracane JL, Berge HX, Condon JR. In vitro aging of dental composites in water--effect of degree of conversion, filler volume, and filler/matrix coupling. J Biomed Mater Res 1998;42:465-472.ArticlePubMed
REFERENCES
Tables & Figures
REFERENCES
Citations
Citations to this article as recorded by 
- Mechanical, Surface and Physicochemical Properties of Nanozeolite‐Modified 3D Printed Hybrid Ceramics at Varying Concentrations: An In Vitro Study
Ahmed A. Holiel, Yomna M. Ibrahim, Noha Morsy
Journal of Esthetic and Restorative Dentistry.2026; 38(2): 325. CrossRef - Color Stability Under Challenge: Effects of Thermo-Aging and Mouthrinse Exposure on Anterior Teeth and Esthetic Composites
Gökçe Keçeci, Zehra Güner, Süleyman Ziya Şenyurt, Kamile Erciyas
European Journal of Therapeutics.2026; 32(1): 94. CrossRef - Evaluation of surface roughness of PEEK and Laser-Sintered cobalt–chromium subjected to different polishing protocols and thermocycling (an in vitro study)
Marzia Kareem Ahmed, Aras Maruf Rauf
Oxford Open Materials Science.2026;[Epub] CrossRef - Comparative influence of triton and cavity conditioners on the surface characteristics and bond strength of dentin, indicating triton as a cavity conditioner
Lena Bal, Cangül Keskin, Aybüke Karaca Sakallı, Bilge Özcan
Journal of Health Sciences and Medicine.2026; 9(1): 98. CrossRef - The Influence of Thermal and Mechanical Aging on the Flexural Properties of Conventional and 3D-Printed Materials Used in Occlusal Splints Manufacturing
Joanna Smardz, Katarzyna Kresse-Walczak, Heike Meißner, Klaus Böning, Joanna Weżgowiec, Andrzej Małysa, Mieszko Więckiewicz
Materials.2026; 19(2): 421. CrossRef - Failure mechanism analysis and machine learning-based residual strength prediction of CFRP with different ply orientations and loading types under six typical accelerated aging environments
Guofeng Qin, Chenglong Su, Peiwen Mi, Peng Huang, Qiuhan Fan, Ming Li, Wei Tan
Construction and Building Materials.2026; 516: 145630. CrossRef - Discoloration, radiopacity, and push-out bond strength of bismuth-based radiopacifiers in endodontic sealers
Mohammad Ali Saghiri, Mina Shekarian, Amir Abdolmaleki, Michael Conte, Steven M. Morgano
Odontology.2026;[Epub] CrossRef - Color matching and metameric behavior of composite resins applied on anodized titanium surfaces: an in vitro spectrophotometric study
Umur Davut, Ozge Doganay-Ozyilmaz, Ozgun Yusuf Ozyilmaz
BMC Oral Health.2026;[Epub] CrossRef - Effect of an Adhesive-Enhancing Primer on Shear Bond Strength in Repairs of Fresh Resin Composite to Aged Resin Composite: With and Without Saliva Contamination
Pemika Lerttiendamrong, Wisarut Prawatvatchara, Suparaksa Yamockul, Awiruth Klaisiri, Tool Sriamporn, Pakpilai Thiranukoon, Niyom Thamrongananskul
Journal of Composites Science.2026; 10(4): 184. CrossRef - An In Vitro Study on Bond Strength Degradation of Low-Shrinkage Composite Resins to Demineralized Dentin After Thermal Cycling
Maria Cristina Borsatto, Barbara Jarreta, Jaciara Miranda Gomes-Silva, Patricia Gatón-Hernández, Carolina Paes Torres, Rodrigo Galo
Oral.2026; 6(2): 41. CrossRef - Engineered micro-textures enhance adhesion in additively manufactured dental crowns
Shiyao Chen, Andrew B. Cameron, John M. Aarts, Joanne J.E. Choi
Digital Dentistry Journal.2026; : 100085. CrossRef - Effect of Simulated Toothbrushing on Surface Roughness, Color Stability, and Gloss of Two Single-Shade Composite Resins
Zeynep Hale Keles, Vasfiye Isik, Soner Sismanoglu
Materials.2026; 19(8): 1523. CrossRef - Clinical Decision‐Making of Repair vs. Replacement of Defective Direct Dental Restorations: A Multinational Cross‐Sectional Study With Meta‐Analysis
Ömer Hatipoğlu, João Filipe Brochado Martins, Mohmed Isaqali Karobari, Nessrin Taha, Thiyezen Abdullah Aldhelai, Daoud M. Ayyad, Ahmed A. Madfa, Benjamin Martin‐Biedma, Rafael Fernández‐Grisales, Bakhyt A. Omarova, Wen Yi Lim, Suha Alfirjani, Kacper Nijak
Journal of Esthetic and Restorative Dentistry.2025; 37(4): 977. CrossRef - An In Vitro Evaluation of Novel Bioactive Liner's Effect on Marginal Adaptation of Class II Composite Restorations: A Scanning Electron Microscope Analysis
Girija S Sajjan, Naveena Ponnada, Praveen Dalavai, Madhu Varma Kanumuri, Venkata Karteek Varma Penmatsa, B V Sindhuja
World Journal of Dentistry.2025; 15(9): 749. CrossRef - Different contemporary resin cements for intracanal luting of glass fiber posts - Bonding and polymerization assessments
Anna Caroliny Detogni, Vitaliano Gomes de Araújo Neto, Caio Felipe de Almeida Nobre, Victor Pinheiro Feitosa, Mário Alexandre Coelho Sinhoreti
International Journal of Adhesion and Adhesives.2025; 138: 103951. CrossRef - Effect of food-simulating liquids and polishing times on the color stability of microhybrid and nanohybrid resin composites
Muhammet Fidan, Nevin Çankaya
Discover Nano.2025;[Epub] CrossRef - Effect of irrigation protocols for post space preparation on the bond of the resin luting agent and post to a hydraulic calcium silicate filled root: An in vitro study
Nuttanun Poeaim, Sirawut Hiran-us, Yanee Tantilertanant
The Journal of Prosthetic Dentistry.2025; 133(4): 1039.e1. CrossRef - Influence of Different Adhesives and Surface Treatments on Shear and Tensile Bond Strength and Microleakage with Micro-CT of Repaired Bulk-Fill Composites
Handan Yıldırım-Işık, Mediha Büyükgöze-Dindar
Polymers.2025; 17(12): 1680. CrossRef - Effect of thermal ageing on physico-mechanical properties and self-healing potential of experimental 3D-printed denture base resin composites
Mariam Raza Syed, Amr Fawzy
Journal of the Mechanical Behavior of Biomedical Materials.2025; 170: 107123. CrossRef - Effects of aging on the physicomechanical, antimicrobial, and cytotoxicity properties of flowable composite resin with strontium-modified phosphate-based glass
Seo-Hyun Kim, Hye-Bin Go, Myung-Jin Lee, Jae-Sung Kwon
Scientific Reports.2025;[Epub] CrossRef - Colour Stability and Optical Properties of Provisional Crowns Fabricated With Milling, 3D Printing, and Direct Technique
Tommaso Rinaldi, Carlos Serrano Granger, Andrea Santamaría Laorden, Jaime Orejas-Perez, Pablo Gómez Cogolludo
International Dental Journal.2025; 75(6): 103932. CrossRef - EVALUATE DEGREE OF CONVERSION OF NEW BIOACTIVE ORTHODONTIC ADHESIVE WITH COLOR CHANGE & FLUORESCENCE PROPERTY
Mohammed Younis, Neam Fakhri Neam Fakhri
BULLETIN OF STOMATOLOGY AND MAXILLOFACIAL SURGERY.2025; : 39. CrossRef - Antibacterial activity and physicochemical properties of light-curable fluoride varnishes containing strontium phosphate-based glass
Na-Yeon Kim, Mi-Sol Ryu, Ji-Min Lee, Soo-Yeon Jeong, Hye-Been Choi, Myung-Jin Lee, Song-Yi Yang
Clinical Oral Investigations.2025;[Epub] CrossRef - Systematic Review of Studies Comparing Microleakage After Restoration With Cention and Conventional Glass Ionomer Cement in Human Extracted Teeth
Rashmi Misra, Mansi Vandekar, Gayatri Pendse, Omkar Bhosale, Pauravi Hegde, Aashaka Vaishnav
Cureus.2025;[Epub] CrossRef - Evaluation of the radiopacity of different universal composite resins aged by thermocycling
Dilber Çölkesen, Alican Kuran, Neslihan Tekçe
Odontology.2025;[Epub] CrossRef - Exploring the sources and routes of micro- and nanoplastics from dental products and materials: their impact on human health - a systematic review
Vidhya Selvaraj, R. Saravanan, N. Raj Vikram, Uma revathi Gopalakrishnan, Ramsamy M
Next Research.2025; 2(4): 100925. CrossRef - Investigation of the mechanical response of MWCNTs infused carbon/glass fiber-based hybrid composites using digital image correlation
Somaiah Chowdary Mallampati, Ujendra Kumar Komal, Paladugu Rakesh, Parthapratim Barman
Construction and Building Materials.2025; 492: 143068. CrossRef - Impact of Graphitic Carbon Nitride on Dental Composite’s Mechanical and Antibacterial Properties
Zainab Rafaqat, Saad Liaqat, Ahmed Bari, Warda Khan Yousafzai, Umar Nishan, Sandleen Feroz, Nawshad Muhammad
Journal of Materials Engineering and Performance.2025;[Epub] CrossRef - Exploring the Biological and Chemical Properties of Emerging 3D-Printed Dental Resin Composites Compared to Conventional Light-Cured Materials
Nikola Živković, Stefan Vulović, Miloš Lazarević, Anja Baraba, Aleksandar Jakovljević, Mina Perić, Jelena Mitrić, Aleksandra Milić Lemić
Materials.2025; 18(22): 5170. CrossRef - Awareness of possible complications associated with direct composite restorations: A multinational survey among dentists from 13 countries with meta-analysis
Anna Lehmann, Kacper Nijakowski, Jakub Jankowski, David Donnermeyer, Paulo J. Palma, Milan Drobac, João Filipe Brochado Martins, Fatma Pertek Hatipoğlu, Indira Tulegenova, Muhammad Qasim Javed, Hamad Mohammad Alharkan, Olga Bekjanova, Sylvia Wyzga, Moataz
Journal of Dentistry.2024; 145: 105009. CrossRef - Comparative evaluation of bond strength and color stability of polyetheretherketone and zirconia layered with indirect composite before and after thermocycling: An in vitro study
Pooja Singh, Subhabrata Maiti, Amrutha Shenoy
The Journal of Indian Prosthodontic Society.2024; 24(3): 252. CrossRef - Biaxial flexural strength of hydrothermally aged resin-based materials
Rodrigo Ricci Vivan, Mariana Miranda de Toledo Piza, Bruna de Mello Silva, Thalya Fernanda Horsth Maltarollo, Gustavo Sivieri-Araujo, Murilo Priori Alcalde, Marco Antonio Hungaro Duarte, Estevam Augusto Bonfante, Henrico Badaoui Strazzi-Sahyon
Journal of the Mechanical Behavior of Biomedical Materials.2024; 155: 106568. CrossRef - Comparative Strength Study of Indirect Permanent Restorations: 3D-Printed, Milled, and Conventional Dental Composites
João Paulo Mendes Tribst, Adelheid Veerman, Gabriel Kalil Rocha Pereira, Cornelis Johannes Kleverlaan, Amanda Maria de Oliveira Dal Piva
Clinics and Practice.2024; 14(5): 1940. CrossRef - Influencia del termociclado sobre la estabilidad del color de dos resinas compuestas
//Influence of thermocycling on the color stability of two composite resins
Verónica Lucía Ventrera, María Eugenia Alejandra Barrionuevo
Revista de la Asociación Odontológica Argentina.2024; : 1. CrossRef - Efeito do protocolo de polimento e do armazenamento em meio úmido na variação de cor, massa e rugosidade superficial de resinas compostas
Leonardo Cruz Morais, Mateus Victória Gontijo, Gabriela Rodrigues Pires, Victor de Morais Gomes, Milton Carlos Kuga, Francisco Fernando Massola Filho, Amanda Gonçalves Franco, Alberto Nogueira da Gama Antunes
Cuadernos de Educación y Desarrollo.2024; 16(6): e4556. CrossRef - A comparison of the mechanical properties of 3D-printed, milled, and conventional denture base resin materials
Hyeong-Ju YU, You-Jung KANG, Yeseul PARK, Hoon KIM, Jee-Hwan KIM
Dental Materials Journal.2024; 43(6): 813. CrossRef - Effect of aging and fiber‐reinforcement on color stability, translucency, and microhardness of single‐shade resin composites versus multi‐shade resin composite
Muhammet Fidan, Özhan Yağci
Journal of Esthetic and Restorative Dentistry.2024; 36(4): 632. CrossRef - Impact of Artificial Aging on the Physical and Mechanical Characteristics of Denture Base Materials Fabricated via 3D Printing
Ahmed Altarazi, Julfikar Haider, Abdulaziz Alhotan, Nick Silikas, Hugh Devlin, Weihao Yuan
International Journal of Biomaterials.2024;[Epub] CrossRef - Synthesis, monomer conversion, and mechanical properties of polylysine based dental composites
Saadia Bano Lone, Rabia Zeeshan, Hina Khadim, Muhammad Adnan Khan, Abdul Samad Khan, Anila Asif
Journal of the Mechanical Behavior of Biomedical Materials.2024; 151: 106398. CrossRef - Bond strength and surface roughness assessment of novel antimicrobial polymeric coated dental cement
Ghada Naguib, Hisham Mously, Jumana Mazhar, Ibrahim Alkanfari, Abdulelah Binmahfooz, Mohammed Zahran, Mohamed T. Hamed
Discover Nano.2024;[Epub] CrossRef - Evaluation of microhardness, degree of conversion, and abrasion resistance of nanoglass and multiwalled carbon nanotubes reinforced three‐dimensionally printed denture base resins
Pansai Ashraf Mohamed, Yomna Mohamed Ibrahim, Kenda Ibrahim Hisham Hanno, Mohamed Mahmoud Abdul‐Monem
Journal of Prosthodontics.2024;[Epub] CrossRef - Effect of CAD-CAM block thickness and translucency on the polymerization of luting materials
Bengü Doğu Kaya, Selinsu Öztürk, Ayşe Aslı Şenol, Erkut Kahramanoğlu, Pınar Yılmaz Atalı, Bilge Tarçın
BMC Oral Health.2024;[Epub] CrossRef - Simulation of oral environmental conditions through artificial aging of teeth for the assessment of enamel discoloration in orthodontics
Celal Irgın
BMC Oral Health.2024;[Epub] CrossRef - Do universal adhesive systems affect color coordinates and color change of single-shade resin composites compared with a multi-shade composite?
Muhammet FİDAN, Özhan YAĞCI
Dental Materials Journal.2023; 42(6): 886. CrossRef - Fabrication, Evaluation, and Performance Ranking of Tri-calcium Phosphate and Silica Reinforced Dental Resin Composite Materials
Sonu Saini, Anoj Meena, Ramkumar Yadav, Amar Patnaik
Silicon.2023; 15(18): 8045. CrossRef - Can Modification with Urethane Derivatives or the Addition of an Anti-Hydrolysis Agent Influence the Hydrolytic Stability of Resin Dental Composite?
Agata Szczesio-Wlodarczyk, Izabela M. Barszczewska-Rybarek, Marta W. Chrószcz-Porębska, Karolina Kopacz, Jerzy Sokolowski, Kinga Bociong
International Journal of Molecular Sciences.2023; 24(5): 4336. CrossRef - Effect of veneering material type and thickness ratio on flexural strength of bi-layered PEEK restorations before and after thermal cycling
Ahmed Gouda, Ashraf Sherif, Mennatallah Wahba, Tarek Morsi
Clinical Oral Investigations.2023; 27(6): 2629. CrossRef - 3D printed denture base material: The effect of incorporating TiO2 nanoparticles and artificial ageing on the physical and mechanical properties
Ahmed Altarazi, Julfikar Haider, Abdulaziz Alhotan, Nick Silikas, Hugh Devlin
Dental Materials.2023; 39(12): 1122. CrossRef - Influence of silane coupling agent and aging on the repair bond strength of dental composites
Gustavo Jusué-Esparza, José Alejandro Rivera-Gonzaga, Guillermo Grazioli, Ana Josefina Monjarás-Ávila, J. Eliezer Zamarripa-Calderón, Carlos Enrique Cuevas-Suárez
Journal of Adhesion Science and Technology.2023; 37(5): 913. CrossRef - Degree of conversion of light‐polymerized composite resin in implant prosthesis screw access opening
Se‐Hyun Park, Yoon‐Hyuk Huh, Chan‐Jin Park, Lee‐Ra Cho, Kyung‐Ho Ko
Journal of Prosthodontics.2023; 32(9): 829. CrossRef - Investigation of the effect of matrix-interface formed with silane-based coupling agents on physico-chemical behavior and flow distance of dental composites
Zerin Yeşil Acar, Merve Tunç Koçyiğit, Meltem Asiltürk
Journal of Molecular Liquids.2023; 378: 121600. CrossRef - Evaluation of Water Sorption and Solubility of 3D-Printed, CAD/CAM Milled, and PMMA Denture Base Materials Subjected to Artificial Aging
Mariya Dimitrova, Angelina Vlahova, Ilian Hristov, Rada Kazakova, Bozhana Chuchulska, Stoyan Kazakov, Marta Forte, Vanja Granberg, Giuseppe Barile, Saverio Capodiferro, Massimo Corsalini
Journal of Composites Science.2023; 7(8): 339. CrossRef - Effect of thermocycling on internal microhardness of high and low viscosity bulk fill composite resins in class I cavities
Sâmara Luciana de Andrade LIMA, Lais Lemos CABRAL, Natália Russo CARLOS, Saulo André de Andrade LIMA, Kamila Rosamilia KANTOVITZ, Flávia Lucisano Botelho do AMARAL
RGO - Revista Gaúcha de Odontologia.2023;[Epub] CrossRef - Effects of an Acidic Environment on the Strength and Chemical Changes of Resin-based Composites
S Kang, B-H Cho
Operative Dentistry.2023; 48(4): E81. CrossRef - Influence of compressive forces and aging through thermocycling on the strength of mono incremental dental composite resins
Cristian Roberto Sigcho Romero, Henry Fabricio Mejía Mosquera, Sandra Marcela Quisiguiña Guevara, Yudy Jacqueline Alvarado Aguayo
Bionatura.2023; 8(4): 1. CrossRef - Push-out Bond Strength of Two Fiber Posts in Composite Resin Using Different Types of Silanization
RM Novis, BLT Leon, FMG França, CP Turssi, RT Basting, FLB Amaral
Operative Dentistry.2022; 47(2): 173. CrossRef - Penetration and Adaptation of the Highly Viscous Zinc-Reinforced Glass Ionomer Cement on Contaminated Fissures: An In Vitro Study with SEM Analysis
Galiah AlJefri, Sunil Kotha, Muhannad Murad, Reham Aljudaibi, Fatmah Almotawah, Sreekanth Mallineni
International Journal of Environmental Research and Public Health.2022; 19(10): 6291. CrossRef - Surface Characteristics and Color Stability of Dental PEEK Related to Water Saturation and Thermal Cycling
Liliana Porojan, Flavia Roxana Toma, Mihaela Ionela Bîrdeanu, Roxana Diana Vasiliu, Ion-Dragoș Uțu, Anamaria Matichescu
Polymers.2022; 14(11): 2144. CrossRef - Effects of aging and light-curing unit type on the volume and internal porosity of bulk-fill resin composite restoration
Afnan O. Al-Zain, Elaf A. Alboloshi, Walaa A. Amir, Maryam A. Alghilan, Eliseu A. Münchow
The Saudi Dental Journal.2022; 34(3): 243. CrossRef - An Evaluation of the Hydrolytic Stability of Selected Experimental Dental Matrices and Composites
Agata Szczesio-Wlodarczyk, Karolina Kopacz, Malgorzata Iwona Szynkowska-Jozwik, Jerzy Sokolowski, Kinga Bociong
Materials.2022; 15(14): 5055. CrossRef - Comparison of the Mechanical Properties and Push-out Bond Strength of Self-adhesive and Conventional Resin Cements on Fiber Post Cementation
MR Santi, RBE Lins, BO Sahadi, JR Soto-Montero, LRM Martins
Operative Dentistry.2022; 47(3): 346. CrossRef - Effect of Different Polymerization Times on Color Change, Translucency Parameter, and Surface Hardness of Bulk-Fill Resin Composites
HY Gonder, M Fidan
Nigerian Journal of Clinical Practice.2022; 25(10): 1751. CrossRef - Surface degradation and biofilm formation on hybrid and nanohybrid composites after immersion in different liquids
Gabriela Escamilla-Gómez, Octavio Sánchez-Vargas, Diana M. Escobar-García, Amaury Pozos-Guillén, Norma V. Zavala-Alonso, Mariana Gutiérrez-Sánchez, José E. Pérez-López, Gregorio Sánchez-Balderas, Gabriel F. Romo-Ramírez, Marine Ortiz-Magdaleno
Journal of Oral Science.2022; 64(4): 263. CrossRef - Effects of Different Adhesive Systems and Orthodontic Bracket Material on Enamel Surface Discoloration: An In Vitro Study
Ali Alqerban, Doaa R. M. Ahmed, Ali S. Aljhani, Dalal Almadhi, Amjad AlShahrani, Hussah AlAdwene, Abdulaziz Samran
Applied Sciences.2022; 12(24): 12885. CrossRef - Effects of Immediate Coating on Unset Composite with Different Bonding Agents to Surface Hardness
Nantawan Krajangta, Supissara Ninbanjong, Sunisa Khosook, Kanjana Chaitontuak, Awiruth Klaisiri
European Journal of Dentistry.2022; 16(04): 828. CrossRef - Rational durability of optical properties of chameleon effect of Omnichroma and Essentia composite thermocycled in black dark drinks (in vitro study)
Bassma Abdelhamed, Asmaa Abdel-Hakeem Metwally, Heba A. Shalaby
Bulletin of the National Research Centre.2022;[Epub] CrossRef - Comparative Evaluation of Shear Bond Strength of Nanohybrid Composite Restoration After the Placement of Flowable Compomer and Composite Using the Snowplow Technique
Meghna Dugar, Anuja Ikhar, Pradnya Nikhade, Manoj Chandak, Nidhi Motwani
Cureus.2022;[Epub] CrossRef - The First Step in Standardizing an Artificial Aging Protocol for Dental Composites—Evaluation of Basic Protocols
Agata Szczesio-Wlodarczyk, Magdalena Fronczek, Katarzyna Ranoszek-Soliwoda, Jarosław Grobelny, Jerzy Sokolowski, Kinga Bociong
Molecules.2022; 27(11): 3511. CrossRef - Effect of Different Surface Treatments on the Long‐Term Repair Bond Strength of Aged Methacrylate‐Based Resin Composite Restorations: A Systematic Review and Network Meta‐analysis
Mahdi Hadilou, Amirmohammad Dolatabadi, Morteza Ghojazadeh, Hossein Hosseinifard, Parnian Alizadeh Oskuee, Fatemeh Pournaghi Azar, Victor Feitosa
BioMed Research International.2022;[Epub] CrossRef - Edge chipping resistance of veneering composite resins
Parissa Nassary Zadeh, Bogna Stawarczyk, Rüdiger Hampe, Anja Liebermann, Felicitas Mayinger
Journal of the Mechanical Behavior of Biomedical Materials.2021; 116: 104349. CrossRef - The effect of radiation exposure and storage time on the degree of conversion and flexural strength of different resin composites
Ragia M. Taher, Lamiaa M. Moharam, Amin E. Amin, Mohamed H. Zaazou, Farid S. El-Askary, Mokhtar N. Ibrahim
Bulletin of the National Research Centre.2021;[Epub] CrossRef - Fracture Load of CAD/CAM Fabricated Cantilever Implant-Supported Zirconia Framework: An In Vitro Study
Ibraheem F. Alshiddi, Syed Rashid Habib, Muhammad Sohail Zafar, Salwa Bajunaid, Nawaf Labban, Mohammed Alsarhan
Molecules.2021; 26(8): 2259. CrossRef - A numerical, theoretical and experimental study of the effect of thermocycling on the matrix-filler interface of dental restorative materials
Yoan Boussès, Nathalie Brulat-Bouchard, Pierre-Olivier Bouchard, Yannick Tillier
Dental Materials.2021; 37(5): 772. CrossRef - Impact of polymerization and storage on the degree of conversion and mechanical properties of veneering resin composites
Felicitas MAYINGER, Marcel REYMUS, Anja LIEBERMANN, Marc RICHTER, Patrick KUBRYK, Henning GROẞEKAPPENBERG, Bogna STAWARCZYK
Dental Materials Journal.2021; 40(2): 487. CrossRef - Intrapulpal Concentration of Hydrogen Peroxide of Teeth Restored With Bulk Fill and Conventional Bioactive Composites
DP Silva, BA Resende, M Kury, CB André, CPM Tabchoury, M Giannini, V Cavalli
Operative Dentistry.2021; 46(3): E158. CrossRef - Silane content influences physicochemical properties in nanostructured model composites
Larissa Maria Cavalcante, Lucielle Guimarães Ferraz, Karinne Bueno Antunes, Isadora Martini Garcia, Luis Felipe Jochims Schneider, Fabrício Mezzomo Collares
Dental Materials.2021; 37(2): e85. CrossRef - AĞIZ GARGARALARI VE ANTİSEPTİKLERİNİN FARKLI KOMPOZİT REZİNLERİN RENK STABİLİTESİNE ETKİSİ
Turan Emre KUZU, Özcan KARATAŞ
Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi.2021; : 1. CrossRef - Evaluation of Immediate and Delayed Microleakage of Class V Cavities Restored with Chitosan-incorporated Composite Resins: An In Vitro Study
Roopa R Nadig, Veena Pai, Arpita Deb
International Journal of Clinical Pediatric Dentistry.2021; 14(5): 621. CrossRef - Influence of Diode Laser for the Treatment of Dentin Hypersensitivity on Microleakage of Cervical Restorations
Doaa R. M. Ahmed, Diana G. Shaath, Jomana B. Alakeel, Abdulaziz A. Samran, Mona Abbassy
BioMed Research International.2021;[Epub] CrossRef - Ageing of Dental Composites Based on Methacrylate Resins—A Critical Review of the Causes and Method of Assessment
Agata Szczesio-Wlodarczyk, Jerzy Sokolowski, Joanna Kleczewska, Kinga Bociong
Polymers.2020; 12(4): 882. CrossRef - Flexural strength and surface microhardness of materials used for temporary dental disocclusion submitted to thermal cycling: An in vitro study
Tamires Borges de Lima, José Guilherme Neves, Ana Paula Terossi de Godoi, Ana Rosa Costa, Viviane Veroni Degan, Américo Bortolazzo Correr, Heloisa Cristina Valdrighi
International Orthodontics.2020; 18(3): 519. CrossRef - Evaluation of the repair capacities and color stabilities of a resin nanoceramic and hybrid CAD/CAM blocks
Hasibe Sevilay Bahadır, Yusuf Bayraktar
The Journal of Advanced Prosthodontics.2020; 12(3): 140. CrossRef - Effect of Different Surface Treatments of Resin Relined Fiber Posts Cemented With Self-adhesive Resin Cement on Push-out and Microtensile Bond Strength Tests
RV Machry, PE Fontana, TC Bohrer, LF Valandro, OB Kaizer
Operative Dentistry.2020; 45(4): E185. CrossRef - Influences of Successive Exposure to Bleaching and Fluoride Preparations on the Surface Hardness and Roughness of the Aged Resin Composite Restoratives
Khalid M. Abdelaziz, Shugufta Mir, Shafait Ullah Khateeb, Suheel M. Baba, Saud S. Alshahrani, Eman A. Alshahrani, Zahra A. Alsafi
Medicina.2020; 56(9): 476. CrossRef - Fracture Resistance of Lithıum Disilicate, Indirect Resin Composite and Zirconıa by Using Dual Cure Resin Cements
Mohammed BADWAN, Erkut KAHRAMANOĞLU
Clinical and Experimental Health Sciences.2020; 10(4): 435. CrossRef - Effect of Stress-decreasing Resin Thickness as an Intermediate Layer on Fracture Resistance of Class II Composite Restoration: An In Vitro Study
Dennis Dennis, Arwin Leonardy, Trimurni Abidin
World Journal of Dentistry.2020; 11(2): 91. CrossRef - Effect of Thermocycling on Biaxial Flexural Strength of CAD/CAM, Bulk Fill, and Conventional Resin Composite Materials
EB Benalcázar Jalkh, CM Machado, M Gianinni, I Beltramini, MMT Piza, PG Coelho, R Hirata, EA Bonfante
Operative Dentistry.2019; 44(5): E254. CrossRef - Mechanical properties of hybrid computer-aided design/computer-aided manufacturing (CAD/CAM) materials after aging treatments
Hae-Yong Jeong, Hae-Hyoung Lee, Yu-Sung Choi
Ceramics International.2018; 44(16): 19217. CrossRef
ePub Link
Cite
XML DownloadThe effect of thermocycling on the degree of conversion and mechanical properties of a microhybrid dental resin composite
Figure 1 Fourier transform infrared spectroscopy (FTIR) spectra of the resin composites before (upper red) and after setting (lower green).
Figure 2 Fourier transform infrared spectroscopy (FTIR) spectra of the resin composites after thermocycling. (A) After 10,000 cycles; (B) After 4,000 cycles; (C) After 1,000 cycles; (D) Baseline after curing.
Figure 3 Scanning electron microscopy (SEM) micrograph of the Filtek Z250 resin composite at ×15,000 magnification. (A) Freshly cured material; (B) After 10,000 cycles of thermocycling; (C) After 14,000 cycles of thermocycling. Coarse protruding filler particles were present in the weakened resin matrix at the thermocycled resin composite surface. Some areas from which filler particles seem to have been debonded and plucked out were observed. The composite showed exposed particles and loosening of filler particles after aging.
Figure 1
Figure 2
Figure 3
The effect of thermocycling on the degree of conversion and mechanical properties of a microhybrid dental resin composite
Composition of organic matrix and filler of Filtek Z250 microhybrid universal dental composite
| Organic matrix | Filler | Manufacturer | Lot No. | ||
|---|---|---|---|---|---|
| Type | Vol (%) | Size (µm) | |||
| Bisphenol A diglycidyl ether dimethacrylate (BisGMA), Urethane dimethacrylate (UDMA), Bisphenol A polyethylene glycol diether dimethacrylate (BisEMA), Camphoroquinone (initiator) | Zirconia/silica | 60 | 0.01–3.5 µm with average of 0.6 µm | 3M ESPE (St. Paul, MN, USA) | N569982 |
Degree of conversion (DC, %) of the thermocycled specimens
| Filtek Z250 | DC (%) | CV (%) |
|---|---|---|
| 24 hr | 61.012 ± 3.694a | 6.05 |
| 1,000 cycles | 61.960 ± 2.360a | 3.81 |
| 2,000 cycles | 64.860 ± 1.577a | 2.43 |
| 4,000 cycles | 68.032 ± 4.641b | 6.82 |
| 6,000 cycles | 68.800 ± 4.544b | 6.60 |
| 8,000 cycles | 68.268 ± 2.695b | 3.95 |
| 10,000 cycles | 67.052 ± 3.312b | 4.94 |
Values of DC are presented as means ± standard deviations. Values marked with different lower-case superscript letters are significantly different (Tukey HSD post hoc test, p < 0.05).
CV, coefficient of variation; HSD, honest significant difference.
Flexural strength (FS) and microhardness of the thermocycled specimens
| Filtek Z250 | FS (MPa) | CV (%) | Microhardness (VHN, kgf/mm2) | CV (%) |
|---|---|---|---|---|
| 24 hr (G1) | 117.044 ± 21.724a | 18.56 | 98.184 ± 6.971a | 7.10 |
| 1,000 cycles (G2) | 90.490 ± 22.732b | 25.12 | 102.135 ± 2.863a | 2.80 |
| 4,000 cycles (G3) | 61.751 ± 10.178c | 16.48 | 84.676 ± 10.669b | 12.60 |
| 10,000 cycles (G4) | 45.824 ± 8.366d | 18.26 | 61.056 ± 3.064c | 5.02 |
Values of FS and microhardness are presented as means ± standard deviations. Values marked with different lower-case superscript letters are significantly different (Tukey HSD post hoc test, p < 0.05).
CV, coefficient of variation; VHN, Vickers hardness number; G1, group 1; G2, group 2; G3, group 3; G4, group 4; HSD, honest significant difference.
Table 1 Composition of organic matrix and filler of Filtek Z250 microhybrid universal dental composite
Table 2 Degree of conversion (DC, %) of the thermocycled specimens
Values of DC are presented as means ± standard deviations. Values marked with different lower-case superscript letters are significantly different (Tukey HSD
CV, coefficient of variation; HSD, honest significant difference.
Table 3 Flexural strength (FS) and microhardness of the thermocycled specimens
Values of FS and microhardness are presented as means ± standard deviations. Values marked with different lower-case superscript letters are significantly different (Tukey HSD
CV, coefficient of variation; VHN, Vickers hardness number; G1, group 1; G2, group 2; G3, group 3; G4, group 4; HSD, honest significant difference.