To evaluate the effect of vital tooth bleaching agent and alcohol pretreatment on dentin bonding, flat dentin windows were produced on the buccal side of the crowns of fifty-five extracted, human premolars. A bleaching gel, Opalescence® with 10% of carbamide peroxide (Ultradent Product, USA) was daily applied on the teeth of three experimental groups for six hours for 10 consecutive days, while teeth of a control group were not bleached. After 6 hours of bleaching gel application, the specimens were washed and stored in saline until the next day application. After application of One-step® dentin bonding agent (Bisco, USA), Z-250® resin (3M-ESPE, USA) was bonded to dentin with a mount jig. Shear bond strength was measured with an Instron machine (Type 4202, Instron Corp., USA) after 24 hours. The results were analyzed using one-way ANOVA and Duncan's multiple range test at p < 0.05.

Immediate bonding group showed significantly lower bond strength than un-bleached control group (p < 0.05).

Ethanol-treated group showed significantly higher bond strength compared to immediate bonding group (p < 0.05). However, the bond strength of the ethanol treatment group was lower than that of the un-bleached control group (p < 0.05).

There were no significant difference in shear bond strength between the 2-week delayed bonding group and the ethanol-treated group (p > 0.05) and between delayed bonding group and un-bleached control group (p > 0.05).

In the condition of the present study, it seems that alcohol pretreatment after bleaching procedure can reduce the adverse effect of vital bleaching agent on dentin bonding.

This study was done to evaluate whether vital bleaching agents could influence on the translucency of the bovine enamel. The anterior bovine teeth that were extracted one day before and without any gross discoloration were obtained and then were preserved in physiologic saline. 6 mm cylindrical tooth specimens were fabricated with diamond puncher perpendicularly on labial surface of bovine tooth. After embedded in transparent acrylic resin with labial surface being exposed, they were cut to a thickness of 1.2 mm with low speed diamond saw (Isomat, Buehler Co., Lake Bluff, IL, USA). They were smoothly ground to 1 mm thickness of enamel with sandpaper. 24 specimens were randomly divided into 3 groups and control group respectively. Opalescence (10% carbamide peroxide, Ultradent, South Jordan, USA), Rembrandt (10% carbamide peroxide, DenMat, USA) and Opalescence F (15% carbamide peroxide with fluoride, Ultradent, USA) were applied on labial sides of the bovine enamel for 7 days (bleaching agents were reapplied every 24 hours) and the opposite surface was contacted to cotton that soaked in distilled water. The control group was soaked in distilled water. Three stimulus value X, Y and Z were evaluated with colorimeter (Color & Color Differencemeter, Model TC-6FX, Tokyo Denshoku Co., Japan) on the labial surface of all specimen three times on white and black background plate before the bleaching agents were applied and on 3rd, 5th and 7th day after applied. The degree of translucency was normally assessed by measuring the inverse property, opacity (contrast ratio).

10% Opalescence, 15% Opalescence-F, and control group showed no significant variation in the translucency of bovine enamel, However Rembrandt decreased the translucency of it (p < 0.01).