The purpose of this study is to compare and to evaluate the effect of pH and lactic acid concentration on the progression of artificial root caries lesion using polarizing microscope, and to evaluate the morphological changes of hydroxyapatite crystals of the demineralized area and to investigate the process of demineralization using scanning electron microscope.

Artificial root caries lesion was created by dividing specimens into 3 pH groups (pH 4.3, 5.0, 5.5), and each pH group was divided into 3 lactic acid concentration groups (25 mM, 50 mM, 100 mM). Each group was immersed in acid buffer solution for 5 days and examined. The results were as follows:

1. Under polarized microscope, the depth of lesion was more effected by the lactic acid concentration rather than the pH.

2. Under scanning electron microscope, dissolution of hydroxyapatite crystals were increased as the lactic acid concentration increased and the pH decreased.

3. Demineralized hydroxyapatite crystals showed peripheral dissolution and decreased size and number within cluster of hydroxyapatite crystals and widening of intercluster and intercrystal spaces as the pH decreased and the lactic acid concentration increased.

4. Under scanning electron microscope evaluation of the surface zone, clusters of hydroxyapatite crystals were dissolved, and dissolution and reattachment of crystals on the surface of collagen fibrils were observed as the lactic acid concentration increased.

5. Under scanning electron microscope, demineralization of dentin occurred not only independently but also with remineralization simultaneously.

In conclusion, the study showed that pH and lactic acid concentration influenced the rate of progression of the lesion in artificial root caries. Demineralization process was progressed from the surface of the cluster of hydroxyapatite crystals and the morphology of hydroxyapatite crystals changed from round or elliptical shape into irregular shape as time elapsed.

The purpose of this study is to compare and to evaluate the effects of the degree of saturation on the progression of artificial root caries lesion.

A total of 8 human premolars without any defects and cracks selected and the cementum were removed and the teeth were cleaned with ultrasonic device and pumice without fluoride.

Each tooth was sectioned into 6 pieces and they were ground with #800 sandpaper until they had a thickness of 200µm. Specimens were applied with nail vanish except for the 2-3 mm window area after application of bonding agent. Under the constant pH, the specimens were divided into 6 groups (degree of saturation; 0.1415, 0.1503, 0.1597, 0.1676, 0.1771, 0.1977). Each group was immersed in acid buffer solution for 1, 2, 3, 5 days under controlled temperature (25℃) and imbibed in water and examined using the polarizing microscope.

The results were as follows

1. Although the degree of saturation of demineralization solution decreased, the depth of penetration in the dentin was constant.

2. Erosion was observed on the surface of all the teeth in the group I, II. In the group III, IV, V, surfaces were not changed. The teeth in the group VI showed the more mineralized surface but not the shape of the dentinal tubules distinctively.

3. In all groups, the lesion progressed rapidly at the first day of the experiment, but increased gradually as time elapsed.

Citations

Citations to this article as recorded by  

• Management of white spots: resin infiltration technique and microabrasion
  Jeong-Hye Son, Bock Hur, Hyeon-Cheol Kim, Jeong-Kil Park
  Journal of Korean Academy of Conservative Dentistry.2011; 36(1): 66.     CrossRef