The purpose of this study was to evaluate the microtensile bond strength (µTBS), failure modes and bonding interfaces of self-etching and three self-adhesive resin cements to dentin and indirect composite resin.

Cylindrical composite blocks (Tescera, Bisco Inc.) were luted with resin cements (PA: Panavia F 2.0, Kuraray Medical Inc., RE: RelyX Unicem Clicker, 3M ESPE., MA: Maxem, Kerr Co., BI: BisCem, Bisco Inc.) on the prepared occlusal dentin surfaces of 20 extracted molars. After storage in distilled water for 24 h, 1.0 mm × 1.0 mm composite-dentin beams were prepared. µTBS was tested at a cross-head speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and Tukey's HSD test. Dentin sides of all fractured specimens and interfaces of resin cements-dentin or resin cements-composite were examined at FE-SEM (Field Emission-Scanning Electron Microscope).

In conclusion, PA and RE showed higher bond strength and closer adaptation than MA and BI when indirect composite blocks were luted to dentin using a self-etching and three self-adhesive resin cements.

The purpose of this study was to evaluate the effect of passive or active application of primer and coat times of bond on the shear bond strength when a self-etching primer adhesive (Clearfil SE Bond) was applied to enamel surface.

Crowns of sixteen human molars were selected. Buccal and lingual enamels of crowns were partially exposed and slabs of 1.2 mm thick were made. They were divided into one of four equal groups (n = 8). Group 1: passive application of Primer and 1 coat of Bond, Group 2: active application of Primer and 1 coat of Bond, Group 3: passive application of Primer and 2 coats of Bond, Group 4: active application of Primer and 2 coats of Bond. Clearfil AP-X was bonded to enamel suface of each group using Tygon tubes. The bonded specimens were subjected to microshear bond strength (uSBS) testing with a crosshead speed of 1 mm/min.

The results of this study were as follows;

The uSBS of Group 1 was the lowest among groups and the uSBS of Group 4 was the highest.

Citations

Citations to this article as recorded by  

• Enamel Bond Strength of Self-Etch Adhesives with Phototherapy Active Application: a Pilot Study
  M. K. Ayar, Ö. Yeşil
  Strength of Materials.2024; 56(3): 669.     CrossRef
• Influence of application methods of one-step self-etching adhesives on microtensile bond strength
  Chul-Kyu Choi, Sung-Ae Son, Jin-Hee Ha, Bock Hur, Hyeon-Cheol Kim, Yong-Hun Kwon, Jeong-Kil Park
  Journal of Korean Academy of Conservative Dentistry.2011; 36(3): 203.     CrossRef
• The effect of various bonding systems on the microtensile bond strength of immediate and delayed dentin sealing
  Jin-hee Ha, Hyeon-Cheol Kim, Bock Hur, Jeong-Kil Park
  Journal of Korean Academy of Conservative Dentistry.2008; 33(6): 526.     CrossRef

The purpose of this study was to evaluate the effect of burs on microleakage of Class V resin restorations when a self-etching primer adhesive was used.

Forty Class V cavities were prepared with four different cutting burs on extracted third molars, and divided into one of four equal groups (n = 10); Group 1-plain cut carbide bur (no. 245), Group 2-cross cut carbide bur (no. 557), Group 3-fine diamond bur (TF-21F), Group 4-standard diamond bur (EX-41).

The occlusal and gingival margin of cavities was located in enamel and dentin, respectively. Cavities were treated with Clearfil SE Bond and restored with Clearfil AP-X. Specimens were thermocycled, immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed leakages at enamel and dentinal margins. Data were analyzed using Mann-Whitney and Wilcoxon signed ranked test.

The results of this study were as follows;

1. At enamel margin, microleakage of group 4 was statistically higher than those of group 1, 2 and 3 (p < 0.01).

2. At dentinal margin, microleakage of group 4 was statistically higher than group 3 (p < 0.01), but group 1 and 2 were not statistically different with group 3 and 4.

3. Enamel microleakage was statistically higher than dentinal microleakage in group 1, 2 and 3 (p < 0.05), but statistical difference between the microleakage of enamel and dentinal margin was not in group 4.

In conclusion, the use of coarse diamond bur showed high microleakage at both enamel and dentinal margin when Clearfil SE Bond was used in class V cavity.

Citations

Citations to this article as recorded by  

• Microshear bond strength of a self-etching primer adhesive to enamel according to the type of bur
  Jin-Ho Jeong, Young-Gon Cho, Myung-Seon Lee
  Journal of Korean Academy of Conservative Dentistry.2011; 36(6): 477.     CrossRef
• Effect of cutting instruments on the dentin bond strength of a self-etch adhesive
  Young-Gon Lee, So-Ra Moon, Young-Gon Cho
  Journal of Korean Academy of Conservative Dentistry.2010; 35(1): 13.     CrossRef